Nkolo wa polymer wu akiwile kusuka eka vinylidene fluoride (VDF) , hexafluoropropylene (HFP) na tetrafluoroethylene (TFE) eka ratio leyi kongomeke ya 40/30/30, leswi humesaka nhlayo yale henhla ya fluorine leyi kumekaka eka FKM ya mabindzu . Matrix leyi yo enta ya fluorocarbon yi endla xisirhelelo xa eneji ya le henhla swinene (< 18 mN m−1) lexi hlongolaka non-polar hydrocarbons , polar ester oils , na swiengeteri swa matimba swofana na methanol kumbe biodiesel. Endlelo ra peroxide-scavenging bisphenol-AF cure ri herisa brittle post-cure embrittlement, leswi nyikaka > 20 MPa matimba ya tensile na 35 kN m−1 matimba yo tear hambi endzhaku ka 1,000 h @ 200 °C . Mbuyelo i compound leyi hanyaka kutlula silicone na HNBR hi 3× eka mvhilopho yin’we ya mahiselo loko yi hlayisa < 3 % volume swell eka IRM903 reference oil.
Tafula ra Swihlawulekisi swa Vukheta (Maendlelo ya ASTM)
| Nhundzu |
Ndlela yo Kambela |
FKM-65B20 Value |
Industry Benchmark |
| Rendzo |
ASTM D792 |
1,82 g cm−3 |
1.80–1.85 |
| Ku nonoka |
ASTM D2240 ya xirhendzevutani |
75 ± 3 Ribuwa ra lwandle A |
70–80 |
| Matimba ya Tensile |
ASTM D412 |
20.5 MPa |
> 18 MPa |
| Ku leha @ Ku wisa |
ASTM D412 |
230 % . |
> 180 % . |
| Seti ya Ntshikelelo (200 °C × 70 h) . |
ASTM D395 |
18 % . |
< 25 % . |
| Ku Pfumala ka Tempele ya le Hansi |
ASTM D2137 |
–25 °C |
–20 °C |
| Ku pfimba ka Vholumo eka Mafurha C (23 °C × 70 h) . |
ASTM D471 |
1.2 % . |
< 5 % . |
| Ku dyuhala eka Moya 250 °C × 70 h |
ASTM D573 |
Ku cinca ka tensile –5 % . |
< –15 % 100 . |
Spectrum ya Switirhisiwa swa Mimovha
Tisisiteme ta Turbocharger
Swirhendzevutana swa Mafurha & SCR
Injhini & Vuhundzisi
Chassis & Maburuku
Ti bladders ta ESP hydraulic accumulator leti lavaka < 0.1 % wa ku nghenelela ka mafurha.
Ti bellows leti yimisiweke hi moya leti lwisanaka na ozone, munyu wa le magondzweni na mati ya maburuku.
Nkongomiso wa Vukorhokeri & Tifomo
Xivumbeko xa Compound : Slab leyi hlanganisiweke ka ha ri emahlweni, strip, kumbe pellet leyi lulameleke ku tshikileriwa, ku hundziseriwa, kumbe ku vumbiwa hi injection.
Xirhendzevutani xa ntolovelo xa ku horisa : 5 min @ 170 °C press + endzhaku ka ku horisa 2 h @ 200 °C (moya) kumbe 30 min @ 230 °C steam eka < 1 % ya swilo leswi humesiwaka.
Swipimelo swa Slab : 300 mm × 300 mm × 10 mm (ya ntolovelo 2–30 mm).
Vutomi bya Xefe : 12 wa tinhweti @ ≤ 25 °C eka aluminium-foil/PE double bag; nitrogen-flushed ku sivela ku hisiwa ka oxidative.
Switifikheti & Ku landzelerisa
ISO 9001:2015 & IATF 16949:2016 leyi tiyisisiweke ya xitirhisiwa xo hlanganisa.
REACH & RoHS 3.0 xitiviso lexi heleleke (SVHC < 0.1 %).
Xiviko xa Xikambelo xa SGS – ku handzuka, sete ya ntshikelelo, ku pfimba ka mafurha (download PDF).
Xitatimende xa Timinerali ta Ntwanano – ku kuma swihlovo leswi nga riki na DRC.
Supply Chain & Logistics
| Muxaka wa Odara |
MOQ |
Nkarhi wo Rhangela Ku |
paka |
Incoterm |
| Xitandi xa Xitoko |
25 wa tikhilogiramu |
7–10 wa masiku |
Nkwama wa PE + khatoni |
EXW Xihlamusela-marito xa Shenzhen |
| Muhlovo wa Custom/Ku nonoka |
250 wa tikhilogiramu |
3–4 wa mavhiki |
Xiphemu lexi pfaleriweke hi vacuum |
FOB Shenzhen hi ku tirhisa |
| Pelletized ku endlela ku Humesiwa |
500 wa tikhilogiramu |
4–5 wa mavhiki |
25 kg ya swikhwama swa foil |
CIF Hamburg |
Bundle with Stainless-Steel Cable Ties
Eka ti turbocharger harnesses leti nga exposed to > 200 °C , pair FKM-65B20 gaskets na ti 316 SS cable ties ta hina leti ringanyetiweke –80 °C ku ya eka +538 °C eka sisiteme yo pfalela ya thermal-chemical leyi heleleke.