Muhlovo: ntima
Ku tiya: 65±5 SHORE A
Xihlawulekisi xa sayizi: xi nga endliwa ngopfu hi ku landza swilaveko swa wena (strip kumbe phepha ro anama)
Xiyimo xa vulcanization: 175°C * 10min Vulcanization ya vumbirhi: 200°C * 4h (2mm standard test piece)
Nhlayo ya oda ya le hansi: 50kg

Muhlovo: Brown
Sisiteme ya vulcanization: bisphenol system
Nhlayo ya fluorine: 68%
Mooney viscosity: ML (1+10) 121°C 50-70
Vukulu: Yinga endliwa swinene (xiphepherhele)
Swiyimo swa vulcanization: 175°C*10min Vulcanization ya vumbirhi: 200°C*4h (2mm standard specimen)
MOQ: 50kg

Muhlovo: Brown (leswi nga endliwaka hi ku landza swilaveko swa wena)
Endlelo ra vulcanization: sisiteme ya peroxide
Nhlayo ya fluorine: 70%
Mooney viscosity: ML (1+10) 121°C 20-40
Vukulu: Yi nga endliwa ngopfu (xiphepherhele)
Swiyimo swa vulcanization: 175°C*10min Vulcanization ya vumbirhi: 200°C*4h (2mm standard specimen)
MOQ: 50kg ya xirhendzevutani

Muhlovo: wa ntima
Sisiteme ya vulcanization: sisiteme ya bisphenol
Nhlayo ya fluorine: 68%
Ku tiya: 70±5 SHORE A
Ku tsindziyela ka Mooney: ML(1+10)121°C 30-50
Nhlamuselo ya vukulu: yi nga endliwa swinene (xiphepherhele)
Xiyimo xa vulcanization: 175°C*10min Vulcanization bya vumbirhi: 200°C*4h (2mm standard test piece)
Nhlayo ya le hansi ya oda: 50kg

Fluoroelastomer i synthetic polymer elastomer leyingana ti athomo ta fluorine eka ti carbon atoms ta chain leyikulu kumbe side chain. Ku nghenisiwa ka ti athomo ta fluorine swinyika rhaba ku tiya swinene eka kuhisa, ku tiya ka oxidation, ku tiya ka oyili, ku lwisana na corrosion xikan’we naku lwisana na ku dyuhala ka xibakabaka, naswona yitirhisiwa ngopfu eka aerospace, aviation, automotive, petroleum na switirhisiwa swale kaya.

Muhlovo: Brown (yi nga endliwa hi ku landza swilaveko swa wena)
Endlelo ra vulcanization: bisphenol system
Nhlayo ya fluorine: 65%
Mooney viscosity: ML (1+10) 121°C 20-40
Vukulu: Yi nga endliwa swinene (xiphepherhele)
Swiyimo swa vulcanization: 175°C*10min Vulcanization ya vumbirhi: 200°C*4h (2mm standard specimen)
MOQ: 50kg ya xirhendzevutani