Esemed | Indikaatorid | ||||||
Hinded | Fv9430 | Fv9440 | Fv9450 | Fv9460 | Fv9470 | Fv9480 | |
Välimuse | Piimjas valge poolläbipaistev | Kollakas | |||||
Spetsiifiline gravitatsioon/ g/ cm3 | ASTM D792 | 1.38 | 1.41 | 1.42 | 1.43 | 1.45 | 1.47 |
Karedus/shorea | ASTM D2240 | 28 | 40 | 48 | 60 | 70 | 80 |
Tõmbetugevus/mpa | ASTM D412 | 10.2 | 9.5 | 9.5 | 10.2 | 9.9 | 8.1 |
Pikenemine vaheajal /% | ASTM D412 | 485 | 494 | 363 | 296 | 241 | 159 |
Pisara tugevus/kn/m | ASTM D624-B | 18 | 26 | 19 | 22 | 21 | 16 |
Tihenduskomplekt (177 ℃*22H) | ASTM D395 | 9 | 8 | 8 | 7 | 8 | 9 |
Vastupidavus/% | ASTM D1054 | 41 | 35 | 46 | 40 | 37 | 39 |
*Soojustakistus | Kõvadusmuutus /kalda a | +2 | +2 | +3 | +2 | +2 | +3 |
Tõmbetugevuse muutus, % | -18 | -17 | -21 | -25 | -20 | -19 | |
Pikenemine vaheaja muutumisel, % | -19 | -16 | -18 | -21 | -16 | -15 | |
Kütus C Mahu muutus/% 23 ℃/72H | ASTM D471 | +22 | +19 | +18 | +19 | +19 | +19 |
Kõvenemistingimus | Lisage 0,7 bis (2+5) osa, ühe astme vulkaniseerimine 170 ℃ × 15min, kaheastmeline vulkaniseerimine: 200 ℃ × 4H. |
Soovitatavad toimingud:
Vulkaniseerimiseks on soovitatav kasutada 0,6 kuni 1 osa bisdipenta keemilisest ainest (2,5-dimetüül-2,5-bis (Tert-butüülperoksü) heksaan).
Kliendid peaksid valima kõige sobivama temperatuuri ja aja kõvenemiseks, tuginedes toote suurusele ja ravimeetodile.
Tootepakend:
See toode ei ole ohtlik, see koosneb selle asemel kaardipakist, plastist ja 10 kilogrammi koti kohta, 2 kotti kasti kohta.
Ladustamise vanus:
Sellel tootel on külm vooluhulk, kotti tuleks vältida, et seda ei kahjustata transpordi ega kasutamise ajal.
Hoidke jahedas, kuivas keskkonnas, mille säilivusaeg on 12 kuud.
Esemed | Indikaatorid | ||||||
Hinded | Fv9430 | Fv9440 | Fv9450 | Fv9460 | Fv9470 | Fv9480 | |
Välimuse | Piimjas valge poolläbipaistev | Kollakas | |||||
Spetsiifiline gravitatsioon/ g/ cm3 | ASTM D792 | 1.38 | 1.41 | 1.42 | 1.43 | 1.45 | 1.47 |
Karedus/shorea | ASTM D2240 | 28 | 40 | 48 | 60 | 70 | 80 |
Tõmbetugevus/mpa | ASTM D412 | 10.2 | 9.5 | 9.5 | 10.2 | 9.9 | 8.1 |
Pikenemine vaheajal /% | ASTM D412 | 485 | 494 | 363 | 296 | 241 | 159 |
Pisara tugevus/kn/m | ASTM D624-B | 18 | 26 | 19 | 22 | 21 | 16 |
Tihenduskomplekt (177 ℃*22H) | ASTM D395 | 9 | 8 | 8 | 7 | 8 | 9 |
Vastupidavus/% | ASTM D1054 | 41 | 35 | 46 | 40 | 37 | 39 |
*Soojustakistus | Kõvadusmuutus /kalda a | +2 | +2 | +3 | +2 | +2 | +3 |
Tõmbetugevuse muutus, % | -18 | -17 | -21 | -25 | -20 | -19 | |
Pikenemine vaheaja muutumisel, % | -19 | -16 | -18 | -21 | -16 | -15 | |
Kütus C Mahu muutus/% 23 ℃/72H | ASTM D471 | +22 | +19 | +18 | +19 | +19 | +19 |
Kõvenemistingimus | Lisage 0,7 bis (2+5) osa, ühe astme vulkaniseerimine 170 ℃ × 15min, kaheastmeline vulkaniseerimine: 200 ℃ × 4H. |
Soovitatavad toimingud:
Vulkaniseerimiseks on soovitatav kasutada 0,6 kuni 1 osa bisdipenta keemilisest ainest (2,5-dimetüül-2,5-bis (Tert-butüülperoksü) heksaan).
Kliendid peaksid valima kõige sobivama temperatuuri ja aja kõvenemiseks, tuginedes toote suurusele ja ravimeetodile.
Tootepakend:
See toode ei ole ohtlik, see koosneb selle asemel kaardipakist, plastist ja 10 kilogrammi koti kohta, 2 kotti kasti kohta.
Ladustamise vanus:
Sellel tootel on külm vooluhulk, kotti tuleks vältida, et seda ei kahjustata transpordi ega kasutamise ajal.
Hoidke jahedas, kuivas keskkonnas, mille säilivusaeg on 12 kuud.