FV9700 fluorosilicone .

Saa ade yi fata ma extrusion molding of bis-disulfide. Ɛwɔ ngo a ɛko tia, solvent a ɛko tia, acid ne alkali a ɛko tia.

Adeɛ	Nsɛnkyerɛnnede ahorow .
	Serial nɔma .	NFS9760 .	NFS9770 .
	Mmaeɛ Akwan a wɔfa so sɔ hwɛ .	a ɛyɛ mmerɛw, ɛyɛ mmerɛw, . Efĩ biara nni hɔ .
Tumi a ɛtwe ade ba fam pɔtee/ g/cm .³	ASTM D792 na ɛwɔ hɔ.	1.44	1.48
Hardness/Shorea .	ASTM D2240 na ɛwɔ hɔ.	60	70
Tensile ahoɔden/MPa .	ASTM D412 na ɛwɔ hɔ.	10.5	10.1
Elongation wɔ ahomegye mu /% .	ASTM D412 na ɛwɔ hɔ.	207	201
Tear ahoɔden/kn/m .	ASTM D624-B .	18	17
Nhyɛso a wɔde hyɛ mu(177 °C*22h) .	Hardness variation/a .	+4.	+5.
	Nsakraeɛ a ɛba wɔ ahoɔden a ɛtwetwe mu/% .	-27	-24
	Nsakraeɛ a ɛba wɔ ntrɛmu mu/% .	-26	-23
Petrol C . Volume nsakrae/% . 23°C/72h .	ASTM D471 na ɛwɔ hɔ.	21	20
IRM903 volumetric rate a ɛyɛ nsakrae/% 150 × 72h .	ASTM D471 na ɛwɔ hɔ.	4.5	4
Nitric Acid/Sulfuric Acid/Hydrochloric Acid Aduru a Wɔde Afra PH a Wɔde Afra Mu 100°C×120H .
Acid resistance volume nsakrae dodow/% .	ASTM D471 na ɛwɔ hɔ.	0.3	0.3
3% sodium hydroxide aduru 60°C × 72h .
alkali resistance volume nsakrae dodow/% .	ASTM D471 na ɛwɔ hɔ.	0.4	0.3
Curing tebea .	Bisditetra afã horow 0.8, vulcanisation a ɛwɔ afã biako 120°C×15min, Vulcanisation a ɛwɔ afã abien: 200 × 4h .

Nneyɛe a wɔkamfo kyerɛ:

Wɔahyɛ nyansa sɛ wɔmfa bisdisulfide afã horow 0.4-0.7 (2,5-dimethyl-2,5-bis(Tert-butylperoxy)hexane) nni dwuma.

Ɛsɛ sɛ adetɔfo paw ɔhyew ne bere a ɛfata sen biara ma ayaresa a egyina ade no kɛse ne ɔkwan a wɔfa so sa yare no so.

Nneɛma a wɔde yɛ nneɛma:

Saa ade yi nyɛ asiane, mmom ɛyɛ cardstock, plastic, ne kilogram 10 wɔ bag biara mu, bag 2 wɔ adaka biara mu.

Mfe a wɔde sie:

Saa adeɛ yi wɔ cold flow capacity, ɛsɛ sɛ wɔkwati bag no sɛdeɛ ɛbɛyɛ a wɔrensɛe no wɔ akwantuo anaa dwumadie mu.

Fa sie baabi a ɛhɔ yɛ nwini na ɛhɔ yɛ kusuu a asram 12 na ɛbɛtra hɔ akyɛ.

Dada:

Deɛ ɛdi hɔ:

Extruded . Extrusion nsusuwso . FVMQ . Fluorosilicone .

FV9600 fluorosilicone .

FV9502 Fluorosilicone .

Fluorosilicone rɔba FV9500 .

Fluorosilicone rɔba FV9400 .

Fluorosilicone rɔba FV9200 .