Chinhu | Zviratidzo | ||
Siriyero nhamba | NFS9760 | NFS9770 | |
Chitarisiko Bvunzo nzira | Translucent, yakatsetseka, Hapana tsvina | ||
Chaiyo gravity / g / cm3 | ASTM D792 | 1.44 | 1.48 |
Hardness / SHOREA | ASTM D2240 | 60 | 70 |
Tensile Simba / MPA | ASTM D412 | 10.5 | 10.1 |
ELOLOLOLINGT PASTRY /% | ASTM D412 | 207 | 201 |
Misodzi yemberi / kn / m | Astm D624-B | 18 | 17 |
Kudzvinyirira Set (177 ℃ * 22h) | Kuomesa / a | +4 | +5 |
Chiyero chekuchinja kweiyo tensile simba /% | -27 | -24 | |
Chiyero chekuchinja kweelongation /% | -26 | -23 | |
Mafuta c Vhoriyamu Shanduko /% 23 ℃ / 72h | ASTM D4771 | 21 | 20 |
Irm903 | ASTM D4771 | 4.5 | 4 |
Nitric acid / sulfutic acid / hydrochloric acid yakasanganiswa mhinduro pH <1 100 × 120h | |||
Acid kuramba | ASTM D4771 | 0.3 | 0.3 |
3% Sodium Hydroxide Solution 60 × 72h | |||
Alkali Kudzivisa | ASTM D4771 | 0.4 | 0.3 |
Kurapa mamiriro | 0.8 zvikamu zveBisditra, imwe-nhanho Vulcanisation 120 × 15min, maviri-nhanho Vulcanisation: 200 × 4h |
Zvikurudzirwa Zviito:
Izvo zvinokurudzirwa kushandisa 0.4-0.7 zvikamu zveBisdisulfide (2,5-dimethyl-2,5-bis (tert-butylperoxy) hexane).
Vatengi vanofanirwa kusarudza tembiricha yakakwana uye nguva yekurapa zvichienderana nehukuru hwechigadzirwa uye nzira yekurapa.
Chigadzirwa Chigadzirwa:
Ichi chigadzirwa hachina njodzi, ndezvekuumbwa kwekaritsti, mapurasitiki, uye gumi makiromita paBag, 2 mabhegi pane bhokisi.
Zera rekuchengetedza:
Ichi chigadzirwa chine chando chinoyerera, bhegi rinofanira kudzivirirwa kuitira kuti rirege kukuvara panguva yekufambisa kana kushandiswa.
Chengetedza munzvimbo inotonhorera, yakaoma mamiriro nehupenyu hwesherufu hwemwedzi gumi nemaviri.
Chinhu | Zviratidzo | ||
Siriyero nhamba | NFS9760 | NFS9770 | |
Chitarisiko Bvunzo nzira | Translucent, yakatsetseka, Hapana tsvina | ||
Chaiyo gravity / g / cm3 | ASTM D792 | 1.44 | 1.48 |
Hardness / SHOREA | ASTM D2240 | 60 | 70 |
Tensile Simba / MPA | ASTM D412 | 10.5 | 10.1 |
ELOLOLOLINGT PASTRY /% | ASTM D412 | 207 | 201 |
Misodzi yemberi / kn / m | Astm D624-B | 18 | 17 |
Kudzvinyirira Set (177 ℃ * 22h) | Kuomesa / a | +4 | +5 |
Chiyero chekuchinja kweiyo tensile simba /% | -27 | -24 | |
Chiyero chekuchinja kweelongation /% | -26 | -23 | |
Mafuta c Vhoriyamu Shanduko /% 23 ℃ / 72h | ASTM D4771 | 21 | 20 |
Irm903 | ASTM D4771 | 4.5 | 4 |
Nitric acid / sulfutic acid / hydrochloric acid yakasanganiswa mhinduro pH <1 100 × 120h | |||
Acid kuramba | ASTM D4771 | 0.3 | 0.3 |
3% Sodium Hydroxide Solution 60 × 72h | |||
Alkali Kudzivisa | ASTM D4771 | 0.4 | 0.3 |
Kurapa mamiriro | 0.8 zvikamu zveBisditra, imwe-nhanho Vulcanisation 120 × 15min, maviri-nhanho Vulcanisation: 200 × 4h |
Zvikurudzirwa Zviito:
Izvo zvinokurudzirwa kushandisa 0.4-0.7 zvikamu zveBisdisulfide (2,5-dimethyl-2,5-bis (tert-butylperoxy) hexane).
Vatengi vanofanirwa kusarudza tembiricha yakakwana uye nguva yekurapa zvichienderana nehukuru hwechigadzirwa uye nzira yekurapa.
Chigadzirwa Chigadzirwa:
Ichi chigadzirwa hachina njodzi, ndezvekuumbwa kwekaritsti, mapurasitiki, uye gumi makiromita paBag, 2 mabhegi pane bhokisi.
Zera rekuchengetedza:
Ichi chigadzirwa chine chando chinoyerera, bhegi rinofanira kudzivirirwa kuitira kuti rirege kukuvara panguva yekufambisa kana kushandiswa.
Chengetedza munzvimbo inotonhorera, yakaoma mamiriro nehupenyu hwesherufu hwemwedzi gumi nemaviri.