FVL-7435
Herchi
| Mavjudligi: | |
|---|---|
| Miqdori: | |
Elementlar |
Sinov usullari |
NFS-L-7435 |
Tashqi ko'rinishi A |
vizual baholash |
sarg'ish |
Tashqi ko'rinishi B |
vizual baholash |
sarg'ish |
Yopishqoqlik / Pa.s A (kesish tezligi 10 s -1 ) |
Q/371002WXH028-2016 |
350 |
Yopishqoqlik / Pa.s B (kesish tezligi 10 s -1 ) |
Q/371002WXH028-2016 |
300 |
25℃×48 soat |
||
O'ziga xos tortishish / g / sm3 |
ASTM D792 |
1.42 |
Qattiqlik / ShoreA |
ASTM D2240 |
35 |
Kuchlanish kuchi/MPa |
ASTM D412 |
8.1 |
Uzilishdagi cho'zilish /% |
ASTM D412 |
320 |
Yirtilish kuchi/KN/m |
ASTM D624-B |
14.5 |
Chidamlilik/% |
ASTM D1054 |
36 |
Siqish to'plami /% (177 ℃ × 22 soat) |
ASTM D395 |
21 |
Yoqilg'i C Ovoz o'zgarishi /% (25 ℃ × 72 soat) |
ASTM D471 |
24.0 |
Foydalanish:
NFS-L-7435 suyuq florosilikon kauchuk ikki komponentli qadoqlangan. Ishlatilganda, A, B komponentlarini 1: 1 aralashtirish va ko'pikni yo'qotish bilan ishlov berishning massa nisbati bo'yicha, 48 soat ichida joylashtirilgan xona harorati (25 ℃ ± 5 ℃) to'liq davolash mumkin.
Qadoqlash:
Plastik barabanga qadoqlangan, har bir A/B komponenti uchun 20 kg.
Saqlash muddati:
Salqin va quruq muhitda, ochilmagan asl qadoqdagi saqlash muddati o'n ikki oy.
Ehtiyot choralari:
Tarkibida azot, oltingugurt, fosfor va ogʻir metallar boʻlgan aralashmalar bilan aloqa qilishdan saqlaning, bu mahsulotning pishmagan yoki vulkanizatsiya qilinmasligiga olib kelishi mumkin.