FVL-7435
Herchy
Kasancewa: | |
---|---|
adadi: | |
Abubuwa |
Hanyoyin gwaji |
Nfs-l-7435 |
Bayyanar a |
Gwaji |
yyashi |
Bayyanin b |
Gwaji |
yyashi |
Danko / pa.s a (Shear Rate 10 S -1 ) |
Q / 371002WXH028-2016 |
350 |
Danko / pa.s b (Shear Rate 10 S -1 ) |
Q / 371002WXH028-2016 |
300 |
25 ℃ × 48h |
||
Takamaiman nauyi / g / cm3 |
Astm D792 |
1.42 |
Hardness / Sheeaa |
Astm D2240 |
35 |
Tenge ƙarfi / MPA |
Astm d412 |
8.1 |
Elongation a karya /% |
Astm d412 |
320 |
Girman hawaye / kn / m |
Astm D624-B |
14.5 |
Rescience /% |
Astm D1054 |
36 |
Kafa /% (177 ℃ × 22h) |
Astm D395 |
21 |
Man c Canjin girma /% (25 ℃ × 72h) |
Astm D471 |
24.0 |
Amfani:
Nfs-L-7435 ruwa filaye yana cushe a cikin bangaren biyu. Lokacin amfani da, a, b bangarorin a daidai da taro rabo na 1: 1 hadawa da lalata magani, zazzabi mai (25 ℃ ± 5 ℃) an sanya shi a cikin 48h za a iya warkewa gaba ɗaya.
Shirya:
Cakuda a cikin dutsen filastik, 20kg ga kowane kayan A / B.
Lokacin ajiya:
Adana a cikin yanayin sanyi da bushewa, ba a buɗe asalin kayan aikin asali na watanni goma sha biyu ba.
Matakan kariya:
Guji hulɗa tare da mahadi da ke ɗauke da nitrogen, sulfur, phosphorus da karafa mai nauyi, wanda zai iya haifar da samfurin ga vurcanisise wanda ba a san shi ba ko kuma ba vulcanisise ba.
Abubuwa |
Hanyoyin gwaji |
Nfs-L-7435 |
Bayyanar a |
Gwaji |
yyashi |
Bayyanin b |
Gwaji |
yyashi |
Danko / pa.s a (Shear Rate 10 S -1 ) |
Q / 371002WXH028-2016 |
350 |
Danko / pa.s b (Shear Rate 10 S -1 ) |
Q / 371002WXH028-2016 |
300 |
25 ℃ × 48h |
||
Takamaiman nauyi / g / cm3 |
Astm D792 |
1.42 |
Hardness / Sheeaa |
Astm D2240 |
35 |
Tenge ƙarfi / MPA |
Astm d412 |
8.1 |
Elongation a karya /% |
Astm d412 |
320 |
Girman hawaye / kn / m |
Astm D624-B |
14.5 |
Rescience /% |
Astm D1054 |
36 |
Kafa /% (177 ℃ × 22h) |
Astm D395 |
21 |
Man c Canjin girma /% (25 ℃ × 72h) |
Astm d471 |
24.0 |
Amfani:
Nfs-L-7435 ruwa filaye yana cushe a cikin bangaren biyu. Lokacin amfani da, a, b bangarorin a daidai da taro rabo na 1: 1 hadawa da lalata magani, zazzabi mai (25 ℃ ± 5 ℃) an sanya shi a cikin 48h za a iya warkewa gaba ɗaya.
Shirya:
Cakuda a cikin dutsen filastik, 20kg ga kowane kayan A / B.
Lokacin ajiya:
Adana a cikin yanayin sanyi da bushewa, ba a buɗe asalin kayan aikin asali na watanni goma sha biyu ba.
Matakan kariya:
Guji hulɗa tare da mahadi da ke ɗauke da nitrogen, sulfur, phosphorus da karafa mai nauyi, wanda zai iya haifar da samfurin ga vurcanisise wanda ba a san shi ba ko kuma ba vulcanisise ba.