FVL-7435
Herçi
| Elýeterliligi: | |
|---|---|
| mukdary: | |
Harytlar |
Synag usullary |
NFS-L-7435 |
Daş görnüşi A. |
wizual baha bermek |
sarymtyl |
Daş görnüşi B. |
wizual baha bermek |
sarymtyl |
Iscapyşmazlyk / Pa.s A. (gyrkym derejesi 10 s -1 ) |
S / 371002WXH028-2016 |
350 |
Iscapyşmazlyk / Pa.s B. (gyrkym derejesi 10 s -1 ) |
S / 371002WXH028-2016 |
300 |
25 ℃ × 48s |
||
Aýratyn agyrlyk güýji / g / sm3 |
ASTM D792 |
1.42 |
Gatylyk / kenar |
ASTM D2240 |
35 |
Dartyş güýji / MPa |
ASTM D412 |
8.1 |
Arakesmede uzalma /% |
ASTM D412 |
320 |
Gözýaşyň güýji / KN / m |
ASTM D624-B |
14.5 |
Çydamlylyk /% |
ASTM D1054 |
36 |
Gysyş toplumy /% (177 ℃ × 22h) |
ASTM D395 |
21 |
Uelangyç C. Sesiň üýtgemegi /% (25 ℃ × 72h) |
ASTM D471 |
24.0 |
Ulanylyşy:
NFS-L-7435 suwuk florosilikon kauçuk iki bölekden ybarat. A, B komponentleri ulanylanda, 1: 1 garyşyk we zaýalanýan bejerginiň köpçülik gatnaşygyna laýyklykda, 48 sagatda ýerleşdirilen otag temperaturasy (25 ℃ ± 5 ℃) doly bejerilip bilner.
Gaplamak:
Plastik deprekde gaplanan, her A / B komponenti üçin 20 kg.
Saklamak möhleti:
Salkyn we gurak gurşawda, on iki aýlap açylmadyk asyl gaplama ammary.
Çäreler:
Azot, kükürt, fosfor we agyr metallary öz içine alýan birleşmeler bilen gatnaşykdan gaça duruň, bu önümiň bişirilmedik ýa-da wulkanizlenmegine sebäp bolup biler.