FVL-7435
Herchy
Upatikanaji: | |
---|---|
Wingi: | |
Vitu |
Njia za mtihani |
NFS-L-7435 |
Kuonekana a |
Tathmini ya kuona |
Njano |
Kuonekana b |
Tathmini ya kuona |
Njano |
Mnato / Pa.S a (kiwango cha shear 10 s -1 ) |
Q/371002WXH028-2016 |
350 |
Mnato / Pa.s b (kiwango cha shear 10 s -1 ) |
Q/371002WXH028-2016 |
300 |
25 ℃ × 48h |
||
Mvuto maalum/g/cm3 |
ASTM D792 |
1.42 |
Ugumu/Shorea |
ASTM D2240 |
35 |
Nguvu tensile/MPA |
ASTM D412 |
8.1 |
Elongation wakati wa mapumziko /% |
ASTM D412 |
320 |
Nguvu ya machozi/kn/m |
ASTM D624-B |
14.5 |
Ustahimilivu/% |
ASTM D1054 |
36 |
Seti ya compression/%(177 ℃ × 22h) |
ASTM D395 |
21 |
Mafuta c Mabadiliko ya kiasi /% (25 ℃ × 72h) |
ASTM D471 |
24.0 |
Matumizi:
Mpira wa fluorosilicone wa NFS-L-7435 umejaa katika sehemu mbili. Wakati wa kutumia, vifaa vya B, kulingana na uwiano wa misa ya 1: 1 kuchanganya na matibabu ya kufifia, joto la kawaida (25 ℃ ± 5 ℃) lililowekwa katika 48h linaweza kuponywa kabisa.
Ufungashaji:
Iliyowekwa kwenye ngoma ya plastiki, 20kg kwa kila sehemu ya A/B.
Kipindi cha Hifadhi:
Imehifadhiwa katika mazingira ya baridi na kavu, kipindi cha uhifadhi cha asili cha ufungaji cha miezi kumi na mbili.
Tahadhari:
Epuka kuwasiliana na misombo iliyo na nitrojeni, kiberiti, fosforasi na metali nzito, ambayo inaweza kusababisha bidhaa hiyo kubatilishwa au sio Vulcanise.
Vitu |
Njia za mtihani |
NFS-L-7435 |
Kuonekana a |
Tathmini ya kuona |
Njano |
Kuonekana b |
Tathmini ya kuona |
Njano |
Mnato / Pa.S a (kiwango cha shear 10 s -1 ) |
Q/371002WXH028-2016 |
350 |
Mnato / Pa.s b (kiwango cha shear 10 s -1 ) |
Q/371002WXH028-2016 |
300 |
25 ℃ × 48h |
||
Mvuto maalum/g/cm3 |
ASTM D792 |
1.42 |
Ugumu/Shorea |
ASTM D2240 |
35 |
Nguvu tensile/MPA |
ASTM D412 |
8.1 |
Elongation wakati wa mapumziko /% |
ASTM D412 |
320 |
Nguvu ya machozi/kn/m |
ASTM D624-B |
14.5 |
Ustahimilivu/% |
ASTM D1054 |
36 |
Seti ya compression/%(177 ℃ × 22h) |
ASTM D395 |
21 |
Mafuta c Mabadiliko ya kiasi /% (25 ℃ × 72h) |
ASTM D471 |
24.0 |
Matumizi:
Mpira wa fluorosilicone wa NFS-L-7435 umejaa katika sehemu mbili. Wakati wa kutumia, vifaa vya B, kulingana na uwiano wa misa ya 1: 1 kuchanganya na matibabu ya kufifia, joto la kawaida (25 ℃ ± 5 ℃) lililowekwa katika 48h linaweza kuponywa kabisa.
Ufungashaji:
Iliyowekwa kwenye ngoma ya plastiki, 20kg kwa kila sehemu ya A/B.
Kipindi cha Hifadhi:
Imehifadhiwa katika mazingira ya baridi na kavu, kipindi cha uhifadhi cha asili cha ufungaji cha miezi kumi na mbili.
Tahadhari:
Epuka kuwasiliana na misombo iliyo na nitrojeni, kiberiti, fosforasi na metali nzito, ambayo inaweza kusababisha bidhaa hiyo kubatilishwa au sio Vulcanise.