Obudde: | |
---|---|
Omuwendo: | |
Okugezesa: Omugerageranyo gwa AB gwa 1 :1, 130°C x 5min x 15MPa
Ebipimo by'ebintu . | ||||
Ekyamaguzi | GA-2040D . |
GA-2040D-45 . |
GA-20400-60 |
|
Endabika | Enzirugavu Omutangaavu/Ekasi/Emmyuufu . | Enzirugavu enzirugavu . | Gray | |
Viscositya (PA·S) . |
250-400 . | 70-100 . | 1500-2000 . |
|
ViscosityB (PA·S) . |
250-400 . | 70-100 . | 1500-2000 . | |
Obukakanyavu (Shorea) . | 43-48 . | 37-43 . | 55-60 . | |
Densite(g/cm 3) . | 1.11 |
1.11 |
1.15 |
|
Amaanyi g’okusika (MPA) . | 7 |
7.0 |
8.5 |
|
okuwanvuwa(%) . | 500 | 450 | 550 | |
Amaanyi g’okukutuka (kn/m) . | 22 |
22 |
35 |
|
Dielectric ekikyukakyuka ku 100Hz . | 3.03 | 2.95 |
3.3 | |
Ensonga y'okusaasaanya AT100Hz . | 0.0016 | 0.0017 | 0.004 | |
Okuziyiza okukulukuta kw’amasannyalaze n’okussaako obubonero . | 1A3.5 . | 1A4.5 . | 1A3.5 . | |
Obuwanvu bw'obusannyalazo (KV/mm) . | 24 .3 . |
20.5 |
22 |
|
Obunene bw’okuziyiza (ω·cm) . | 1.0 *10 .15 | 1.0 *10 .15 | 1.0 *10 .15 | |
Ekibiina ky'ennimi z'omuliro . | FV-0 . | FV-0 . | FV-0 . |
Okugezesa: Omugerageranyo gwa AB gwa 1 :1, 130°C x 5min x 15MPa
Ebipimo by'ebintu . | ||||
Ekyamaguzi | GA-2040D . |
GA-2040D-45 . |
GA-20400-60 |
|
Endabika | Enzirugavu Omutangaavu/Ekasi/Emmyuufu . | Enzirugavu enzirugavu . | Gray | |
Viscositya (PA·S) . |
250-400 . | 70-100 . | 1500-2000 . |
|
ViscosityB (PA·S) . |
250-400 . | 70-100 . | 1500-2000 . | |
Obukakanyavu (Shorea) . | 43-48 . | 37-43 . | 55-60 . | |
Densite(g/cm 3) . | 1.11 |
1.11 |
1.15 |
|
Amaanyi g’okusika (MPA) . | 7 |
7.0 |
8.5 |
|
okuwanvuwa(%) . | 500 | 450 | 550 | |
Amaanyi g’okukutuka (kn/m) . | 22 |
22 |
35 |
|
Dielectric ekikyukakyuka ku 100Hz . | 3.03 | 2.95 |
3.3 | |
Ensonga y'okusaasaanya AT100Hz . | 0.0016 | 0.0017 | 0.004 | |
Okuziyiza okukulukuta kw’amasannyalaze n’okussaako obubonero . | 1A3.5 . | 1A4.5 . | 1A3.5 . | |
Obuwanvu bw'obusannyalazo (KV/mm) . | 24 .3 . |
20.5 |
22 |
|
Obunene bw’okuziyiza (ω·cm) . | 1.0 *10 .15 | 1.0 *10 .15 | 1.0 *10 .15 | |
Ekibiina ky'ennimi z'omuliro . | FV-0 . | FV-0 . | FV-0 . |