Test: AB ratio na 1 :1, 130°C x 5min x 15MPa
Prodakt Paramita dɛn . | ||||
Sɔntin | GA-2040D na di . | GA-2040D-45 we de sho. | GA-20400-60. | |
Aw a luk | layt grey/kamel/rɛd . | Layt grey . | Gre | |
Viscositya (PA·S) | 250-400 na di | 70-100 na di | 1500-2000 na di | |
ViscosityB (PA·S) | 250-400 na di | 70-100 na di | 1500-2000 na di | |
Hadnɛs (Shorea) . | 43-48 Di wan dɛn we de wok. | 37-43 we dɛn bin de yuz. | 55-60 na di . | |
Densiti(g/cm 3) . | 1.11 | 1.11 | 1.15 | |
Tensil Strɔng (MPA) . | 7 | 7.0 | 8.5 | |
Elongeshɔn(%) . | 500 | 450 | 550 | |
Strɔng fɔ wata (KN/M) . | 22 | 22 | 35 | |
Dielektrik konstant na 100Hz . | 3.03 | 2.95 | 3.3 | |
Dissipeshɔn faktɔ na100Hz . | 0.0016 | 0.0017 | 0.004 | |
Resistance to ilektrikal lik ɛn mak . | 1A3.5 Di wan dɛn we de wok. | 1A4.5 Di wan dɛn we de wok. | 1A3.5 Di wan dɛn we de wok. | |
Dielectricstrength (kv/mm) | 24 .3. | 20.5 | 22 | |
Volumeresistity (ω·cm) . | 1.0 *10 we dɛn bin de yuz fɔ mek di fim.15 | 1.0 *10 we dɛn bin de yuz fɔ mek di fim.15 | 1.0 *10 we dɛn bin de yuz fɔ mek di fim.15 | |
Flaym klas . | FV-0 na di . | FV-0 na di . | FV-0 na di . |
Test: AB ratio na 1 :1, 130°C x 5min x 15MPa
Prodakt Paramita dɛn . | ||||
Sɔntin | GA-2040D na di . | GA-2040D-45 we de sho. | GA-20400-60. | |
Aw a luk | layt grey/kamel/rɛd . | Layt grey . | Gre | |
Viscositya (PA·S) | 250-400 na di | 70-100 na di | 1500-2000 na di | |
ViscosityB (PA·S) | 250-400 na di | 70-100 na di | 1500-2000 na di | |
Hadnɛs (Shorea) . | 43-48 Di wan dɛn we de wok. | 37-43 we dɛn bin de yuz. | 55-60 na di . | |
Densiti(g/cm 3) . | 1.11 | 1.11 | 1.15 | |
Tensil Strɔng (MPA) . | 7 | 7.0 | 8.5 | |
Elongeshɔn(%) . | 500 | 450 | 550 | |
Strɔng fɔ wata (KN/M) . | 22 | 22 | 35 | |
Dielektrik konstant na 100Hz . | 3.03 | 2.95 | 3.3 | |
Dissipeshɔn faktɔ na100Hz . | 0.0016 | 0.0017 | 0.004 | |
Resistance to ilektrikal lik ɛn mak . | 1A3.5 Di wan dɛn we de wok. | 1A4.5 Di wan dɛn we de wok. | 1A3.5 Di wan dɛn we de wok. | |
Dielectricstrength (kv/mm) | 24 .3. | 20.5 | 22 | |
Volumeresistity (ω·cm) . | 1.0 *10 we dɛn bin de yuz fɔ mek di fim.15 | 1.0 *10 we dɛn bin de yuz fɔ mek di fim.15 | 1.0 *10 we dɛn bin de yuz fɔ mek di fim.15 | |
Flaym klas . | FV-0 na di . | FV-0 na di . | FV-0 na di . |