Test: A/B ratio na 1 :1, 130°C x 5min x 15MPa
Prodakt Paramita dɛn . | |||||
Sɔntin | GA-2135-15. | GA-2135-25. | GA-2135-35. | GA-2135-45. | |
Aw a luk | Translucent . | ||||
Viskɔsiti(pa.s) . | 60 | 30 | 38 | 30 | |
Hadnɛs (Shorea) . | 18 | 26 | 35 | 48 | |
Densiti(g/cm3) . | 1.03 | 1.06 | 1.06 | 1.10 | |
Tensil Strɔng (MPA) . | 2.5 | 2.8 | 4.2 | 5.5 | |
Elongeshɔn(%) . | 400 | 380 | 330 | 250 | |
Strɔng fɔ wata (KN/M) . | 8 | 9.5 | 11.5 | 16 | |
Linearshrinkage(%) we de na di . | 1.7 | 1.7 | 1.7 | 1.7 |
Test: A/B ratio na 1 :1, 130°C x 5min x 15MPa
Prodakt Paramita dɛn . | |||||
Sɔntin | GA-2135-15. | GA-2135-25. | GA-2135-35. | GA-2135-45. | |
Aw a luk | Translucent . | ||||
Viskɔsiti(pa.s) . | 60 | 30 | 38 | 30 | |
Hadnɛs (Shorea) . | 18 | 26 | 35 | 48 | |
Densiti(g/cm3) . | 1.03 | 1.06 | 1.06 | 1.10 | |
Tensil Strɔng (MPA) . | 2.5 | 2.8 | 4.2 | 5.5 | |
Elongeshɔn(%) . | 400 | 380 | 330 | 250 | |
Strɔng fɔ wata (KN/M) . | 8 | 9.5 | 11.5 | 16 | |
Linearshrinkage(%) we de na di . | 1.7 | 1.7 | 1.7 | 1.7 |