GA-11 × 1 .
Herchy .
bj.bj. | |
---|---|
Tiiša | |
Teko: 1% ya moemedi wa go fodiša (50% paste ya DBPMH ka silicone gum),175° x 5min x 15MPa.
Ditekanyetšo tša Setšweletšwa . | ||||||
Setšweletšwa | GA-11331 . |
GA-1141 . | GA-1151 . | GA-1161 . | GA-1171 . | GA-1181 . |
Ponagalo | Translucent . | |||||
Williamplasticity . |
115 |
150 |
205 |
240 |
280 |
260 |
Go thatafala (Sorea) . |
30 |
40 |
50 |
60 |
70 |
80 |
Kitlano (G / CM3) . | 1.10 |
1.12 |
1.16 |
1.19 |
1.22 |
1.23 |
TensileMatla a go ba le matla (MPA) . |
7 |
8.5 |
8.5 |
8.5 |
7.5 |
7.5 |
go telefa (%) . | 700 |
550 |
450 |
400 |
300 |
200 |
Matla a Megokgo (KN/M) . | 15 |
19 |
20 |
19 |
19 |
19 |
Teko: 1% ya moemedi wa go fodiša (50% paste ya DBPMH ka silicone gum),175° x 5min x 15MPa.
Ditekanyetšo tša Setšweletšwa . | ||||||
Setšweletšwa | GA-11331 . |
GA-1141 . | GA-1151 . | GA-1161 . | GA-1171 . | GA-1181 . |
Ponagalo | Translucent . | |||||
Williamplasticity . |
115 |
150 |
205 |
240 |
280 |
260 |
Go thatafala (Sorea) . |
30 |
40 |
50 |
60 |
70 |
80 |
Kitlano (G / CM3) . | 1.10 |
1.12 |
1.16 |
1.19 |
1.22 |
1.23 |
TensileMatla a go ba le matla (MPA) . |
7 |
8.5 |
8.5 |
8.5 |
7.5 |
7.5 |
go telefa (%) . | 700 |
550 |
450 |
400 |
300 |
200 |
Matla a Megokgo (KN/M) . | 15 |
19 |
20 |
19 |
19 |
19 |