Rabara ya fluorosilicone FV9200 .

Diaetheme	Ditšhupetšo .
	Mephato ya .	FV9240000000000000000000000000000000000000ly	FV9250 .	FV9260 .
	Mekgwa ya teko / Ponagalo .	Lebese le letšo le letšo le le sekileng .
Maatlakgogedi a itšego/ g/cm .3	ASTM D792 .	1.42	1.44	1.45
Go thatafala/maswabi .	ASTM D2240 .	40	50	60
Matla a go goga/MPA .	ASTM D412 .	10.1	10.2	10.3
Elongation ka khefu /% .	ASTM D412 .	490	457	440
Matla a Meokgo/KN/M .	A a l m D 6 2 2 4 - B .	35	42	43
Sete ya kgatelelo (177 ° C * 22H) .	ASTM D395 .	11	11	12
*Kganetšo ya phišo 225°C × 72h	Phetogo ya go thatafala /shore a .	+3 .	+3 .	+2.
	Phetogo ya maatla a go goga, % .	-19	-16	-17
	Elongation ka phetogo ya go kgaotša, % .	-14	-17	-18
Mafura a C . Phetogo ya bophagamo/% . 23 ° C/72h .	ASTM D471 .	23	21	20
Boemo bja go fodiša .	0,7 dBPH, tobetsa pheko: 170 × 15min,Post pheko: 200 × 4h

Ditiro tše di Kgothaleditšwego:

It’s suggested to utilize 0.6 go ya go karolo ya 1 ya moemedi wa dikhemikhale wa Bisdipenta bakeng sa vulcanization (2,5-dimethyl-2,5-bis(tert-butylpexy)hexane).

Bareki ba swanetše go kgetha themperetšha ya maleba kudu le nako ya go fodiša go ya ka bogolo bja setšweletšwa le mokgwa wa go fodiša.

Diphuthelwana tša Setšweletšwa: .

Setšweletšwa se ga se kotsi, go e na le moo se bopilwe ka cardstock, polasetiki, le dikhilograma tše 10 ka mokotla, mekotla ye 2 ka lepokisi.

Mengwaga ya Polokelo: .

Setšweletšwa se se na le bokgoni bja go elela bja go tonya, mokotla o swanetše go efoga gore o se ke wa senywa nakong ya dinamelwa goba tšhomišo.

Boloka tikologong ye e fodilego, ye e omilego ka bophelo bja šelefo ya dikgwedi tše 12.