Fluorosilicone kawotchou FV9200

Atik	Endikatè
	Klas	FV9240	FV9250	FV9260
	Metòd tès / Aparans	Lakte blan translusid
Gravite espesifik / g / cm3	ASTM D792	1.42	1.44	1.45
Dite/shoreA	ASTM D2240	40	50	60
Fòs rupture/MPa	ASTM D412	10.1	10.2	10.3
Elongasyon nan kraze /%	ASTM D412	490	457	440
Chire fòs/KN/m	ASTM D624-B	35	42	43
Konpresyon ansanm (177℃ * 22h)	ASTM D395	11	11	12
* Rezistans chalè 225 ℃ × 72h	Chanjman dite / rivaj A	+3	+3	+2
	Chanjman fòs rupture, %	-19	-16	-17
	Elongasyon nan chanjman repo, %	-14	-17	-18
Gaz C Chanjman Volim/% 23℃/72h	ASTM D471	23	21	20
Kondisyon geri	0.7 DBPH, gerizon pou laprès: 170℃ × 15min, Post geri: 200℃ × 4h

Aksyon rekòmande:

Li sijere pou itilize 0.6 a 1 pati nan ajan chimik bisdipenta pou vulkanizasyon (2,5-dimethyl-2,5-bis (tert-butylperoxy)hexane).

Kliyan yo ta dwe chwazi tanperati ki pi apwopriye ak tan pou geri ki baze sou gwosè pwodwi a ak metòd pou geri.

Anbalaj pwodwi:

Pwodui sa a pa danjere, li konpoze olye de kat, plastik, ak 10 kilogram pou chak sak, 2 sache pou chak bwat.

Laj nan depo:

Pwodui sa a gen yon kapasite koule frèt, sak la ta dwe evite yo nan lòd yo pa gen li domaje pandan transpò oswa itilizasyon.

Kenbe nan yon anviwònman fre, sèk ak yon lavi etajè nan 12 mwa.