Fluoroélastomère ezalí élastomère polymère synthétique oyo ezali na ba atome ya fluor na ba atome ya carbone ya monyololo monene to ya monyololo ya mopanzi. Kokotisa ba atome ya fluor epesaka caoutchouc résistance excellente na chaleur, résistance na oxydation, résistance na mafuta, résistance na corrosion mpe résistance ya vieillissement atmosphérique, mpe esalelamaka mingi na aérospatiale, aviation, automobile, pétrole mpe ba appareils ya ndako.

Bozali:

Motango:



Botuna . Bobakisa na kitunga .

Composé ya caoutchouc fluoroélastomère-FKM

Biloko ya caoutchouc FKM ezali na résistance excellente ya température ya likolo, résistance na corrosion chimique, résistance na mafuta, performance ya déformation permanente ya malamu, résistance na flamme mpe perméabilité ya gaz.

Fluoroélastomère esalelamaka mingi mingi na bokangami ya température ya likolo mpe ya nse, bisaleli mpe bisaleli na vide, bisaleli ya chimique, mituka, aviation mpe makambo mosusu.

Herchy Rubber ezali na équipe professionnelle ya R&D pona ko répondre na ba besoins ya personnalisation ya ba clients na biso.

●Système ya vulcanisation ya bisphénol na système ya vulcanisation ya peroxyde

●Kobongisa mpe kobimisa biloko mpo na moulage, injection, extrusion mpe ba méthodes mosusu ya traitement.

●Personnaliser composé fluoroélastomère na duresse 50-90 degrés, ba couleurs ndenge na ndenge na ba applications selon ba besoins ya ba clients.

HERCHY .	Lolenge ya vulcanisation	Fluor oyo ezali na kati	Viscosité ya Mooney .	Kotonda	Bokasi ya kokangama	Elongation na tango ya pause	TR10	Ensemble ya compression	Ndenge ya kosalela	Ezaleli
								200°C * 72h ASTM D395 Lolenge B
Bapoint		% .	ML(1+10)121°C	g/cm3	Mp	% .	°C	% .
FKM-65B20	Bisphenol oyo ezali na kati	65.9	20	1.8	12.3	170	-17	17	O-rings;Jonette ya kosala	Ensemble ya compression ya nse; Liquidité ya malamu;
FKM-65B40 oyo ezali na kati	Bisphenol oyo ezali na kati	65.9	40	1.81	14.3	180	-17	16	O-rings;Jonette ya kosala	Force mécanique ya likolo; Ensemble ya compression ya nse
FKM-65B60 oyo ezali na kati	Bisphenol oyo ezali na kati	65.9	60	1.81	15.5	180	-17	16	O-rings;Jonette ya kosala	Force mécanique ya likolo; Ensemble ya compression ya nse
FKM-68B40 oyo ezali na kati	Bisphenol oyo ezali na kati	68.5	40	1.85	14.3	220	-14	26	O-rings;Jonette ya kosala	Liquidité ya malamu; Résistance excellent na ba médias chimiques; Resistance ya température ya likolo
FKM-68B60 oyo ezali na kati	Bisphenol oyo ezali na kati	68.5	60	1.85	16.2	200	-14	26	O-rings;Jonette ya kosala	Force mécanique ya likolo; Resistance excellent na ba médias chimiques; Resistance ya température ya likolo
FKM-65B30S oyo ezali na kati	Bisphenol oyo ezali na kati	65.9	30	1.80	15.0	190	-20	21	Biloko oyo esalemi na extrudé, biloko oyo ekɔtisami na nzoto, biloko oyo esalemi na biloko oyo esalemi na biloko	Résistance ya température ya se; Force mécanique ya likolo; Liquidité ya malamu;
FKM-70P30 oyo ezali na kati	Peroxyde oyo ezali na kati	70	30	1.9	18.5	220	-7	36	Biloko oyo esalemi na extrudé, biloko oyo ekɔtisami na nzoto, biloko oyo esalemi na biloko oyo esalemi na biloko	Liquidité ya malamu; Résistance excellent acide na alcalin; Résistance excellent na ba médias chimiques; Resistance ya température ya likolo
FKM-68P45	Peroxyde oyo ezali na kati	68	45	1.85	16.5	280	-16	36	Biloko oyo esalemi na extrudé, biloko oyo ekɔtisami na nzoto, biloko oyo esalemi na biloko oyo esalemi na biloko	Liquidité ya malamu; Résistance excellent acide na alcalin; Résistance excellent na ba médias chimiques; Resistance ya température ya likolo