GA-91x33.
Herchy .
Go hwetšagala: | |
---|---|
Bogolo: | |
Teko: 1% ya moemeli curing (50% peista ya DBPMH ka silicone marenete), 175 ° x5minx15Mpa
Ditekanyetšo tša Setšweletšwa . | |||||
Setšweletšwa | GA-9133 . |
GA-9143 . | GA-9153 . | GA-9163 . | GA-9173 . |
Ponagalo | Translucent . | ||||
Go thatafala (Sorea) . |
30 |
40 |
50 |
60 |
70 |
Kitlano (G / CM3) . | 1.08 |
1.12 |
1.14 |
1.16 |
1.18 |
Matla a go goga (MPA) . |
3.5 |
4.0 |
5.0 |
6.0 |
6.0 |
go telefa (%) . | 550 |
550 |
450 |
350 |
200 |
Matla a Meokgo (KN/M) . | 10 |
14 |
16 |
16 |
16 |
Kganetšo ya bokagodimo (ω) . |
108--10 .9 |
Teko: 1% ya moemeli curing (50% peista ya DBPMH ka silicone marenete), 175 ° x5minx15Mpa
Ditekanyetšo tša Setšweletšwa . | |||||
Setšweletšwa | GA-9133 . |
GA-9143 . | GA-9153 . | GA-9163 . | GA-9173 . |
Ponagalo | Translucent . | ||||
Go thatafala (Sorea) . |
30 |
40 |
50 |
60 |
70 |
Kitlano (G / CM3) . | 1.08 |
1.12 |
1.14 |
1.16 |
1.18 |
Matla a go goga (MPA) . |
3.5 |
4.0 |
5.0 |
6.0 |
6.0 |
go telefa (%) . | 550 |
550 |
450 |
350 |
200 |
Matla a Meokgo (KN/M) . | 10 |
14 |
16 |
16 |
16 |
Kganetšo ya bokagodimo (ω) . |
108--10 .9 |