Color: Brown
Vulcanization system: bisphenol system
Fluorine content: 68%
Mooney viscosity: ML (1+10) 121°C 50-70
Size: Can be more customized (sheet)
Vulcanization conditions: 175°C*10min Secondary vulcanization: 200°C*4h (2mm standard specimen)
MOQ: 50kg

Color: Brown (customizable)
Vulcanization system: peroxide system
Fluorine content: 70%
Mooney viscosity: ML (1+10) 121°C 20-40
Size: Can be more customized (sheet)
Vulcanization conditions: 175°C*10min Secondary vulcanization: 200°C*4h (2mm standard specimen)
MOQ: 50kg

Color: black
Vulcanization system: bisphenol system
Fluorine content: 68%
Hardness: 70±5 SHORE A
Mooney viscosity: ML(1+10)121℃ 30-50
Size specification: can be more customized (sheet)
Vulcanization condition: 175℃*10min Secondary vulcanization: 200℃*4h (2mm standard test piece)
Minimum order quantity: 50kg

Color: Brown (customizable)
Vulcanization system: bisphenol system
Fluorine content: 65%
Mooney viscosity: ML (1+10) 121°C 20-40
Size: Can be more customized (sheet)
Vulcanization conditions: 175°C*10min Secondary vulcanization: 200°C*4h (2mm standard specimen)
MOQ: 50kg

Fluoroelastomer is a synthetic polymer elastomer containing fluorine atoms on the carbon atoms of the main chain or side chain. The introduction of fluorine atoms gives rubber excellent heat resistance, oxidation resistance, oil resistance, corrosion resistance and atmospheric aging resistance, and is widely used in aerospace, aviation, automotive, petroleum and household appliances.

Color: black
Hardness: 65±5 SHORE A
Size specification: can be more customized (strip or wide sheet)
Vulcanization condition: 175℃*10min Secondary vulcanization: 200℃*4h (2mm standard test piece)
Minimum order quantity: 50kg