Koulè: Brown
Vulkanizasyon Sistèm: Bisphenol Sistèm
Fliyò Kontni: 68%
Mooney Viskozite: ML (1+10) 121 ° C 50-70
Size: Ka plis Customized (Fèy)
Kondisyon Vulkanizasyon: 175 ° C*10min Segondè Vulcanization: 200 ° C*4h (2mm echantiyon estanda) MOQ: 50KG: 50 ° C*4h (2mm echantiyon estanda) MOQ: 50KG: 50 ° C*4H (2mm echantiyon estanda) MOQ: MOQ: 50 KOK: 50 ° C*4H (2mm echantiyon estanda) MOQ: MOQ: 50 KOK: 50 ° C*4H (2mm echantiyon estanda) MOQ: MOQ: 50 ° C*4h (2mm echantiyon estanda) MOQ: MOQ: 50 KOK: 50 ° C*4H (2mm echantiyon estanda)
MOQ: MOQ: REYG:.

Color: Brown (customizable)
Vulcanization system: peroxide system
Fluorine content: 70%
Mooney viscosity: ML (1+10) 121°C 20-40
Size: Can be more customized (sheet)
Vulcanization conditions: 175°C*10min Secondary vulcanization: 200°C*4h (2mm standard specimen)
MOQ: 50kg

Color: black
Vulcanization system: bisphenol system
Fluorine content: 68%
Hardness: 70±5 SHORE A
Mooney viscosity: ML(1+10)121℃ 30-50
Size specification: can be more customized (sheet)
Vulcanization condition: 175℃*10min Secondary vulcanization: 200℃*4h (2mm standard test piece)
Minimum order quantity: 50kg

Color: black
Vulcanization system: bisphenol system
Hardness: 70±5 SHORE A
Mooney viscosity: ML(1+10)121℃ 50-70
Size specification: can be more customized (sheet)
Vulcanization conditions: 175℃*10min Secondary vulcanization: 200℃*4h (2mm standard test piece)
Minimum order quantity: 50kg

Koulè: Brown (Customizable)
Vulkanizasyon Sistèm: Bisphenol Sistèm
Fliyò Kontni: 65%
Mooney Viskozite: ML (1+10) 121 ° C 20-40
Size: Ka plis Customized (Fèy)
Vulkanizasyon Kondisyon: 175 ° C*10min Segondè Vulkanizasyon: 200 ° C*4h (2mm Standard Specim)
Estandè) 50 ° C.

Fluoroelastomer se yon elastomèr polymère sentetik ki gen atòm fliyò sou atòm yo kabòn nan chèn prensipal la oswa chèn bò. Entwodiksyon nan atòm fliyò bay kawotchou rezistans chalè ekselan, rezistans oksidasyon, rezistans lwil oliv, rezistans korozyon ak atmosferik aje rezistans, epi li se lajman ki itilize nan avyon, aviyasyon, otomobil, petwòl ak aparèy nan kay la.