Loko: mainty
Hatezerana: 65±5 SHORE A
Famaritana ny habeny: azo amboarina kokoa (strip na taratasy mivelatra)
Toe-javatra vulcanization: 175 ℃ * 10min vulcanization faharoa: 200 ℃ * 4h (sokajim-panadinana mahazatra 2mm)
Famandrihana kely indrindra: 50kg

Loko: volontsôkôlà
rafitra Vulcanization: rafitra bisphenol
Votoatin'ny fluorine: 68%
Mooney viscosity: ML (1+10) 121°C 50-70
Habe: Azo amboarina kokoa (tabilao)
fepetran'ny vulcanization: 175°C*10min Fanaovana vulkanika faharoa: 200°C*5h (2mm standard)
MOQ

Loko: Brown (azo amboarina)
Rafitra vulcanisation: rafitra peroxide
Votoatin'ny fluorine: 70%
Viscosity Mooney: ML (1+10) 121°C 20-40
Habe: Azo amboarina kokoa (tabilao)
Fepetra vulcanization: 175°C*10min Volcanization faharoa: 200°C*
4h5h

Loko: mainty
rafitra Vulcanization: rafitra bisphenol
Votoatin'ny fluorine: 68%
Hardness: 70±5 SHORE A
Mooney viscosity: ML (1 + 10) 121 ℃ 30-50
Famaritana ny habeny: azo amboarina kokoa (tabilao)
Toetran'ny vulcanization: 175 ℃ * 10min Faharoa vulcanization: 200 ℃ farany ambany
: 20 ℃ 50 kg

Fluoroelastomer dia elastomer polymère sentetika misy atôma fluorine amin'ny atoma karbaona amin'ny rojo lehibe na rojo an-daniny. Ny fampidirana atôma fluorine dia manome fingotra tsara amin'ny hafanana, ny fanoherana ny oksidia, ny fanoherana ny solika, ny fanoherana ny harafesina ary ny fanoherana ny fahanterana amin'ny atmosfera, ary ampiasaina betsaka amin'ny aerospace, fiaramanidina, fiara, solika ary fitaovana an-trano.

Loko: Brown (azo amboarina)
Rafitra vulcanisation: rafitra bisphenol
Votoatin'ny fluorine: 65%
Viscosity Mooney: ML (1+10) 121°C 20-40
Habe: Azo amboarina kokoa (tabilao) Fepetra momba ny vulcanization: 175°C*10min Volcanization faharoa
200°C*4hmen (200°C)
: