GA-11 × 3
Herchy
Upatikanaji: | |
---|---|
Wingi: | |
Mtihani: 1% ya wakala wa kuponya (kuweka 50% ya DBPMH katika ufizi wa silicone), 175 ° C x 5min x 15MPA.
Vigezo vya bidhaa | ||||||
Bidhaa | GA-1133 |
GA-1143 | GA-1153 | GA-1163 | GA-1173 | GA-1183 |
Kuonekana | Translucent | |||||
Williamplasticity |
115 |
150 |
205 |
240 |
280 |
310 |
Ugumu (Shorea) |
30 |
40 |
50 |
60 |
70 |
80 |
Uzani (g/cm3) | 1.10 |
1.12 |
1.16 |
1.19 |
1.22 |
1.22 |
Tensilestrength (MPA) |
7.5 |
7.5 |
9 |
8.5 |
8.5 |
7.5 |
Elongation (%) | 700 |
500 |
450 |
400 |
300 |
200 |
TAFAKARI (KN/M) | 16 |
20 |
20 |
20 |
20 |
16 |
Mtihani: 1% ya wakala wa kuponya (kuweka 50% ya DBPMH katika ufizi wa silicone), 175 ° C x 5min x 15MPA.
Vigezo vya bidhaa | ||||||
Bidhaa | GA-1133 |
GA-1143 | GA-1153 | GA-1163 | GA-1173 | GA-1183 |
Kuonekana | Translucent | |||||
Williamplasticity |
115 |
150 |
205 |
240 |
280 |
310 |
Ugumu (Shorea) |
30 |
40 |
50 |
60 |
70 |
80 |
Uzani (g/cm3) | 1.10 |
1.12 |
1.16 |
1.19 |
1.22 |
1.22 |
Tensilestrength (MPA) |
7.5 |
7.5 |
9 |
8.5 |
8.5 |
7.5 |
Elongation (%) | 700 |
500 |
450 |
400 |
300 |
200 |
TAFAKARI (KN/M) | 16 |
20 |
20 |
20 |
20 |
16 |