GA-9041 .
Herchy .
Sɔrɔli: | |
---|---|
Hakɛ: | |
Kɔrɔbɔli: Platinum vulcanizing agent, 130°C x 5min x 15MPa.
Product Paramɛtɛrɛw . | |||||
Ka kɛ | GA-9041 . |
GA-9051 . | GA-9061 . | GA-9071 . | GA-9081 . |
Yecogo | Jɛlen | ||||
WilliamPlasticity . |
190 |
210 |
240 |
270 |
290 |
Gɛlɛya (Shoaa) . |
40 |
50 |
60 |
70 |
80 |
density(G/CM3) . | 1.13 |
1.16 |
1.18 |
1.19 |
1.21 |
Tensile fanga (MPa) . |
9.0 |
10.0 |
10.0 |
9.5 |
9.0 |
elongation(%) . | 900 |
700 |
600 |
500 |
400 |
Ɲɛjibɔ fanga (KN/M) . | 30 |
35 |
35 |
35 |
35 |
Kɔrɔbɔli: Platinum vulcanizing agent, 130°C x 5min x 15MPa.
Product Paramɛtɛrɛw . | |||||
Ka kɛ | GA-9041 . |
GA-9051 . | GA-9061 . | GA-9071 . | GA-9081 . |
Yecogo | Jɛlen | ||||
WilliamPlasticity . |
190 |
210 |
240 |
270 |
290 |
Gɛlɛya (Shoaa) . |
40 |
50 |
60 |
70 |
80 |
density(G/CM3) . | 1.13 |
1.16 |
1.18 |
1.19 |
1.21 |
Tensile fanga (MPa) . |
9.0 |
10.0 |
10.0 |
9.5 |
9.0 |
elongation(%) . | 900 |
700 |
600 |
500 |
400 |
Ɲɛjibɔ fanga (KN/M) . | 30 |
35 |
35 |
35 |
35 |