GA-9041 .
Herchy .
Go hwetšagala: | |
---|---|
Bogolo: | |
Teko: platinamo vulcanizing moemeli, 130 ° C x 5min x 15Mpa.
Ditekanyetšo tša Setšweletšwa . | |||||
Setšweletšwa | GA-9041 . |
GA-9051 . | GA-9061 . | GA-9071 . | GA-9081 . |
Ponagalo | Pepeneneng | ||||
Williamplasticity . |
190 |
210 |
240 |
270 |
290 |
Go thatafala (Sorea) . |
40 |
50 |
60 |
70 |
80 |
Kitlano (G / CM3) . | 1.13 |
1.16 |
1.18 |
1.19 |
1.21 |
Matla a go goga (MPA) . |
9.0 |
10.0 |
10.0 |
9.5 |
9.0 |
go telefa (%) . | 900 |
700 |
600 |
500 |
400 |
Matla a Meokgo (KN/M) . | 30 |
35 |
35 |
35 |
35 |
Teko: platinamo vulcanizing moemeli, 130 ° C x 5min x 15Mpa.
Ditekanyetšo tša Setšweletšwa . | |||||
Setšweletšwa | GA-9041 . |
GA-9051 . | GA-9061 . | GA-9071 . | GA-9081 . |
Ponagalo | Pepeneneng | ||||
Williamplasticity . |
190 |
210 |
240 |
270 |
290 |
Go thatafala (Sorea) . |
40 |
50 |
60 |
70 |
80 |
Kitlano (G / CM3) . | 1.13 |
1.16 |
1.18 |
1.19 |
1.21 |
Matla a go goga (MPA) . |
9.0 |
10.0 |
10.0 |
9.5 |
9.0 |
go telefa (%) . | 900 |
700 |
600 |
500 |
400 |
Matla a Meokgo (KN/M) . | 30 |
35 |
35 |
35 |
35 |