Fluorosilicone Caoutchouc FV9500 .

Produit oyo ebongi pona production ya tuyau ya turbocompresseur ya voiture to tuyau composite misusu na ba produits misusu.
Excellent performance ya calendrier, performance ya liaison co-curée na caoutchouc ya silicone
excellente résistance ya mafuta, résistance na solvant.

Modele:
FV9500
Marke:
HERCHY .

Disponibilité:

Quantité:



Botuna . Bobakisa na kitunga .

Boyebisi ya biloko .

Ba indicateurs techniques .

Biloko	Ba indicateurs .
	Bapoint	FV9540	FV9550	FV9560	FV9561
	Komonana Ba méthodes ya test .	Jaune ya .
Gravité spécifique/ g/cm .³	ASTM D792	1.40	1.41	1.42	1.44
Bokasi/Seshorea .	ASTM D2240 .	41	50	60	61
Bokasi ya kokangama/MPA .	ASTM D412	9.5	9.8	10.2	9.8
Elongation na pause /% .	ASTM D412	370	282	263	310
Bokasi ya mayi ya miso/KN/M .	ASTM D624-B .	17	17	18	17
*Botelemeli ya molunge 225°C×72h	Bokasi ya makasi /shore A .	+4.	+2.	+2.	+2.
	Mbongwana ya makasi ya kokangama, % .	-24	-25	-23	-26
	Elongation na changement ya pause, % .	-19	-10	-14	-12
Essence C . Mbongwana ya volume/% . 23°C/72h .	ASTM D471	+23 .	+23 .	+21 .	+21 .
Bokasi ya peel/n/mm, na caoutchouc ya silicone ya vinyle méthyl .		2.0	2.0	2.2	2.0
Ezalela ya kobikisa .	Bobakisa 0,8 biteni ya vulcanisation bis-di-quaternaire, na étape moko 120°C, vulcanisation ya ba étapes mibale: 200°C

Résistance supérieure na ba environnements ya makasi : Caoutchouc FV9500 Fluorosilicone eleki na ba environnements na températures ya makasi mpe na exposition na ba produits chimiques agressifs. Ezali kopesa botɛmɛli malamu mpenza mpo na esansi, mafuta, mpe biloko ndenge na ndenge, mpe yango esalaka ete ezala malamu mpo na kosɛnga yango na baizini.
Température ya monene : Matériel oyo epesaka température ya mosala ya monene, kobanda na -60°C kino na likolo lokola 200°C. Yango esalaka ete ezala malamu mingi mpo na kosalela yango na baizini ya mituka, ya aérospatiale, mpe ya kosala biloko, epai ba fluctuations ya température ezali mingi.
Excellent Compression Set Resistance : FV9500 elakisaka résistance ya kokamwa na ensemble ya compression, ko assurer performance prolongée mpe efficacité ya scellement na pression soutenue, même na ba conditions ya stress makasi.
Bowumeli ya kobakisama : Composition ya fluorosilicone ematisaka bowumeli na bowumeli, ozone, mpe botalisami ya UV, kosala ete bondimi mpe bosali ya ntango molai, ata na ba conditions ya makasi ya zinga zinga.
Isolation électrique supérieure : epesaka ba propriétés ya isolation électrique excellente, yango wana ezali idéal mpo na kosalela na ba composants électroniques mpe ba applications ya scellement esika résistance électrique ezali cruciale.
Versatilité na application : Matériel ekoki kosalelama na ba industries ndenge na ndenge, na kati na yango mituka, aérospatiale, pétrole na gaz, mpe électronique, mpo na kosangisa makasi ya mécanique mpe résistance chimique.
Flexibilité ya malamu mpe résistance ya mayi ya miso : Caoutchouc ya fluorosilicone FV9500 epesaka flexibilité ata na ba températures ya nse, esangisi na excellente ya résistance ya mayi ya miso mpe ya abrasion, ko assurer performance ya kozala na confiance na ba conditions dynamiques mpe ya kolata ya likolo.
Ba options ya grade ya biloko ya kolia ezali : Na kotalela masengi na yo, ba variantes ya caoutchouc ya fluorosilicone ekoki kozala formulé mpo na kokokisa ba normes ya grade ya biloko ya kolia, kopesa solution ya sécurité mpo na ba applications na traitement ya biloko ya kolia mpe na ba industries pharmaceutiques.