Utafiti juu ya moshi wa chini na halogen moto wa bure retardant ethylene propylene mpira wa kuhami.

Maoni: 0     Mwandishi: Mhariri wa Tovuti Chapisha Wakati: 2023-08-13 Asili: Tovuti

Kuuliza

Ethylene propylene mpira (EPR), pamoja na mpira wa binary ethylene propylene mpira na ternary ethylene propylene mpira (EPDM) aina mbili, ni mpira uliojaa, na insulation bora ya umeme, unyevu, joto, baridi na kuzeeka, hutumika sana katika utayarishaji wa waya na nyaya, na imekuwa njia ya muundo wa mwili. With the increasingly high requirements of the laying environment, wire and cable are being developed towards low-smoke halogen-free flame retardant, with the same low-pressure grades of cross-linked polyethylene, EPR also belongs to the flammable materials, its own molecular composition and structure of the flame retardant performance has little effect, only with a considerable amount of flame retardant in order to achieve the purpose of flame Retardant, kwa hivyo ili kufanya vifaa vya chini vya moto vya halogen-bure vinaweza kuongezwa tu kwenye darasa la bure la halogen la retardants za moto. Uchunguzi umeonyesha kuwa mali ya umeme ya EPDM inaathiriwa sana na moto wa moto, ongeza tu sehemu 80 za moto wa hydroxide utafanya kupungua kwa haraka kwa umeme, ili kufikia IEC 60502 ((iliyokadiriwa voltage ya 1 ~ 30 kV iliyoingizwa kwa vifuniko vya kawaida vya viboreshaji vya njia ya kawaida ya viboreshaji vya njia ya kawaida. > Moshi wa chini wa moto wa halogen-bure-retardant EPR ya kuhami zaidi kwa miaka, wakati hafla zilizojaa kama njia ndogo na majengo ya juu yanahitaji kurudishwa kwa moto kwa insulation ya cable na sheath ili kuboresha usalama wa moto. Pamoja na teknolojia ya urekebishaji wa uso wa viboreshaji vya moto wa isokaboni kama vile hydroxide ya alumini na hydroxide ya magnesiamu na utafiti na maendeleo ya njia mpya za uzalishaji, inawezekana kukidhi mahitaji hapo juu.


1 Athari za aina ya moto ya isokaboni juu ya utendaji wa vifaa vya chini vya moto vya halogen-bure


Nguvu tensile ya EPDM kuhami vifaa vya wambiso na hydroxide ya magnesiamu ni kubwa zaidi, haswa kutokana na ukweli kwamba

Magnesiamu hydroxide ni fuwele-kama sindano, saizi ya chembe chini ya 2μm, na kupitia muundo wa wakala wa coupling wa silika ili kuongeza nguvu ya kumfunga na utangamano wa hydroxide ya magnesiamu na EPDM. Kwa kulinganisha index ya oksijeni na kiwango cha mwako wa wima, inaweza kuonekana kuwa athari ya moto ya magnesiamu hydroxide ni bora zaidi kuliko ile ya hydroxide ya alumini, hii ni kwa sababu ya joto la juu ya joto la juu ya joto la juu la joto la aluminium kwa kiwango cha juu cha joto la 140 kwa sababu ya joto la alumini. the processing process, moreover magnesium hydroxide will form a layer of oxidized film adsorbed on the surface of the adhesive material after dehydration and promote the formation of charcoal, which will form a layer of hard shell on the surface of the adhesive material In addition, after dehydration, magnesium hydroxide will form a layer of oxidized film adsorbed on the surface of rubber material, and promote the formation of Carbon, kutengeneza ganda ngumu kwenye uso wa nyenzo za mpira, ikitenga oksijeni, na hivyo kuboresha mfumo wa moto. Ulinganisho wa urekebishaji wa kiasi unaweza kuhitimishwa, hydroxide ya aluminium kwenye mpira wa insulation wa EPDM ethylene propylene (EPR), pamoja na mpira wa ethylene propylene mpira na ternary ethylene propylene mpira (EPDM) aina mbili, ni mpira uliojaa, na insulation bora ya umeme, inaandaliwa kwa kasi, ni ya kutumiwa kwa nguvu, ni pamoja na kutumiwa kwa cabl, ni comping ared incupled and and is is is is is is is is is is is is is is is is is is is is is is is is is is is is is a. Mbadala kamili kwa mwili kuu wa mpira wa styrene-butadiene kama nyenzo ya insulation ya cable. With the increasingly high requirements of the laying environment, wire and cable are being developed towards low-smoke halogen-free flame retardant, with the same low-pressure grades of cross-linked polyethylene, EPR also belongs to the flammable materials, its own molecular composition and structure of the flame retardant performance has little effect, only with a considerable amount of flame retardant in order to achieve the purpose of flame Retardant, kwa hivyo ili kufanya vifaa vya chini vya moto vya halogen-bure vinaweza kuongezwa tu kwenye darasa la bure la halogen la retardants za moto. Uchunguzi umeonyesha kuwa mali ya umeme ya EPDM inaathiriwa sana na moto wa moto, ongeza tu sehemu 80 za moto wa hydroxide utafanya kupungua kwa haraka kwa umeme, ili kufikia IEC 60502 ((iliyokadiriwa voltage ya 1 ~ 30 kV iliyoingizwa kwa vifuniko vya kawaida vya viboreshaji vya njia ya kawaida ya viboreshaji vya njia ya kawaida. > Moshi wa chini wa moto wa halogen-bure-retardant EPR ya kuhami zaidi kwa miaka, wakati hafla zilizojaa kama njia ndogo na majengo ya juu yanahitaji kurudishwa kwa moto kwa insulation ya cable na sheath ili kuboresha usalama wa moto. Pamoja na teknolojia ya urekebishaji wa uso wa viboreshaji vya moto wa isokaboni kama vile hydroxide ya alumini na hydroxide ya magnesiamu na utafiti na maendeleo ya njia mpya za uzalishaji, inawezekana kukidhi mahitaji hapo juu.


1. Ushawishi wa aina ya moto wa isokaboni juu ya utendaji wa moshi wa chini wa moto wa halogen-free retardant EPDM Insulation Mpira


Nguvu tensile ya EPDM kuhami vifaa vya wambiso na hydroxide ya magnesiamu ni kubwa zaidi, haswa kutokana na ukweli kwamba hydroxide ya magnesiamu ni fuwele-kama sindano, saizi ya chembe chini ya 2μM, na kupitia muundo wa wakala wa coupling wa Silane ili kuongeza nguvu ya kumfunga na utangamano wa hydroxide na ePDMide. Kwa kulinganisha index ya oksijeni na kiwango cha mwako wa wima, inaweza kuonekana kuwa athari ya moto ya magnesiamu hydroxide ni bora zaidi kuliko ile ya hydroxide ya alumini, hii ni kwa sababu ya joto la juu ya joto la juu ya joto la juu la joto la aluminium kwa kiwango cha juu cha joto la 140 kwa sababu ya joto la alumini. the processing process, moreover magnesium hydroxide will form a layer of oxidized film adsorbed on the surface of the adhesive material after dehydration and promote the formation of charcoal, which will form a layer of hard shell on the surface of the adhesive material In addition, after dehydration, magnesium hydroxide will form a layer of oxidized film adsorbed on the surface of rubber material, and promote the formation of Carbon, kutengeneza ganda ngumu kwenye uso wa nyenzo za mpira, ikitenga oksijeni, na hivyo kuboresha mfumo wa moto. Ulinganisho wa urekebishaji wa kiasi unaweza kuhitimishwa, hydroxide ya aluminium kwenye EPDM insulation ya vifaa vya umeme vya insulation ya athari ya athari ni ndogo sana kuliko hydroxide ya magnesiamu, hii ni kwa sababu mwenendo wa ATH 104E sio zaidi ya 60 ps-cm ~; na hydroxide ya kawaida ya magnesiamu, kama vile aina ya njia ya uzalishaji, kwa sababu ya chanzo cha ndani cha ushawishi wa mgodi, maudhui ya hali ya juu, usafi wa chini, kwa kuongeza uso wake na malipo mazuri, polarity ya juu, mkazo wa ndani wa microscopic, ili uwepo wa hadi 250 ps. 1 au zaidi, idadi kubwa ya hydroxide ya magnesiamu iliyoongezwa kwenye nyenzo za mpira wa EPDM itafanya mali ya kuhami ya mpira ilipungua sana, ingawa hydroxide ya magnesiamu baada ya matibabu maalum ya kurekebisha uso inaweza kuboresha mali ya kuhami ya nyenzo za mpira, lakini matokeo bado sio bora. Kuzingatia kiwango sawa cha hydroxide ya magnesiamu ina mali bora ya kurudisha moto kuliko hydroxide ya alumini, sisi na wazalishaji wa magnesium hydroxide kwa pamoja huboresha viashiria vya mwili vya magnesiamu hydroxide, aina ya modifiers ya uso na njia za uzalishaji, na hutengeneza aina mbili za umeme za umeme za umeme za epiudium epiumi. na MH3005 na MH3005Z.


Mpira wa kuhami wa MH3005 na MH3005Z EPDM una kiwango cha juu cha kiwango cha juu, ambacho msingi wa kuhami uliotengenezwa na mpira wa MH3005Z kimsingi unakidhi mahitaji ya IEC 60502, lakini mali ya kuhami ya mpira wa MH3005 ni ya juu. Walakini, utendaji wa insulation wa msingi uliotengenezwa na mpira wa MH3005 ni chini, na inakadiriwa kuwa muundo wa uso wa msingi uliharibiwa wakati wa mchakato wa uboreshaji wa extrusion, na sababu inahitaji kuchunguzwa zaidi.


Kwa jumla, ikilinganishwa na mpira wa insulation wa EPDM na hydroxide ya magnesiamu iliyobadilishwa peke yake na EPDM insulation Rubber na aluminium hydroxide peke yake, ya zamani ina mali nzuri ya kurudisha moto, nguvu ya juu, na mali bora ya kuhami baada ya urekebishaji maalum, lakini bado kuna hatari ya kuharibika kwa mali isiyohamishika, lakini kuna mali ya kuhamasisha, wakati wa uhamishaji wa mali, lakini kuna mali ya kuhami, lakini ni hatari ya kuhami, lakini ni hatari ya kuhamasisha, wakati wa uhamishaji wa mali, lakini ni hatari ya kuhamasisha, wakati wa kuhami wahamasi Resisition inaweza kukidhi mahitaji hata bila muundo.


2. Athari za retardants ya moto ya isokaboni juu ya utendaji wa moshi wa chini, halogen-free flame retardant EPDM adhesives ya kuhami


Matumizi moja ya magnesiamu hydroxide au alumini hydroxide isokaboni ya moto haiwezi kukidhi wakati huo huo mahitaji ya mali ya umeme na mali ya moto, kwa hivyo hydroxide ya alumini na magnesium hydroxide na athari yake juu ya utendaji wa chini-smoke halogene-fretant-epardent epame-epardent epamentment-addeantment-fretantment epardem-fretant-fretantment-fretant-fretant-fretant-fretant-fretant-fretant-fretant-fretant-fretant-fretant-fretant-fretant-fretant-fretant-fretant-fretant-fretant-fretant-fretant-fretant-fretant-fretant-fretant-fretant-fretant-fretant. Kipimo cha MH3005Z cha jumla ya sehemu 120, na kuongezeka kwa kipimo cha MH3005Z, mnato wa Menni na nguvu tensile ya wambiso wa kuhami wa EPDM iliongezeka, mali za moto ziliongezeka, utaftaji wa kiasi ulipungua. Pamoja na ongezeko la MH3005Z, mnato wa Menni na nguvu tensile ya kuongezeka kwa wambiso wa EPDM, mali ya moto huongezeka, na upungufu wa kiasi hupungua. Wakati uwiano wa ATH 104E/MH3005Z ni 90/30, mali ya kuhami na moto ya wambiso ya kuhami ya EPDM inakidhi mahitaji. Ulinganisho wa ATH 104E / MH3005Z na uwiano wa kesi 110/10 na 120 / LO, ingawa ongezeko la sehemu 10 za ATH 104E baada ya mali ya wambiso wa wambiso wa EPDM imeboreshwa, lakini mali ya kupungua kwa haraka. LATH 104E / MH3005Z na uwiano wa kesi 70/50 na 70/40, kupunguza sehemu 10 za MH3005Z ingawa inaweza kuboresha mali ya insulation ya mpira, lakini mali za moto hazifikii mahitaji. Ili kuhakikisha kuwa mali ya kurudisha moto, jumla ya moto wa moto hauwezi kupunguzwa.


EPDM Insulation Rubber nyenzo za moshi zisizo na nyuzi ni 355 au hivyo, na kiwango cha moto wa isokanic na bila uhusiano dhahiri na uwiano, hii ni kwa sababu ya formula ya vifaa vyote, malezi ya moshi ni EPDM, ingawa haitoi moshi wa moshi.


3. Wakala wa Kupunguza Moshi juu ya Utendaji wa Kiwanja cha Kuingiza Halogen-Halogen-Bure-Retardant EPDM


JB / T 10707-2007 'Thermoplastic halogen isiyo na moshi wa chini wa Moto wa Moto wa Moto ' inahitaji kwamba wiani wa moshi usio na joto wa nyenzo za mpira haupaswi kuwa mkubwa kuliko 250, ili kupunguza wiani wa moshi wa vifaa vya mpira lazima uongezwe kwa kukandamiza moshi. Montmorillonite ina kalsiamu-msingi, msingi wa sodiamu, montmorillonite ya msingi wa magnesiamu, baada ya kuvua na utawanyiko, utakaso na muundo, mchanganyiko maalum wa kikaboni, unene wa wastani wa safu ni chini ya 25 nm. Montmorillonite imechaguliwa kufikia athari bora ya moshi.


Montmorillonite juu ya ePDM insulation mpira wa vifaa vya moshi wa athari ni dhahiri sana, lakini pia inaweza kuwa ongezeko ndogo la mali ya kurudisha moto, wakati mali zingine zina athari kidogo; Pamoja na kuongezeka kwa kiasi cha montmorillonite, EPDM insulation mpira wa vifaa moshi wa moshi hupungua polepole, na huwa na utulivu, kwa kuzingatia sababu za gharama, chagua kiasi cha montmorillonite kwa sehemu 5.


4 Hitimisho

.

.

.


Viungo vya haraka

Bidhaa zetu

Maelezo ya mawasiliano

Ongeza: No.33, Lane 159, Barabara ya Taiye, Wilaya ya Fengxian, Shanghai
Tel / whatsapp / skype: +86 15221953351
Barua pepe:  info@herchyrubber.com
Hakimiliki     2023 Shanghai Herchy Rubber Co, Ltd. Sitemap |   Sera ya faragha | Msaada na Leadong.