Is rubar próipiléine eitiléine (EPR) é, lena n-áirítear rubar próipiléine dénártha eitiléine agus rubar próipiléine eitiléine trínártha (EPDM), rubar sáithithe, le hinsint leictreach den scoth, taise, teas, frithsheasmhacht fhuar agus aosaithe, is é an t-ábhar a úsáidtear go forleathan i gcáblaí agus i gcáblaí a bheith ina n-árachas cuimsitheach. With the increasingly high requirements of the laying environment, wire and cable are being developed towards low-smoke halogen-free flame retardant, with the same low-pressure grades of cross-linked polyethylene, EPR also belongs to the flammable materials, its own molecular composition and structure of the flame retardant performance has little effect, only with a considerable amount of flame retardant in order to achieve the purpose of flame retardant, so in order to make Ní féidir ábhair lasair-saor ó halaigine íseal-halaigine a chur leis an aicme lasair lasair saor ó halaigine. Studies have shown that the electrical properties of EPDM is greatly affected by the flame retardant, just add 80 parts of hydroxide flame retardant will make the rapid decline in electrical resistivity, in order to achieve the IEC 60502 ((rated voltage of 1 ~ 30 kV extruded insulated cables and their accessories) standards in the EPR insulating rubber in the normal operation of the conductor at the highest temperature of the insulation Friotaíocht /> 3.67 MΩ -km agus Friotaíocht Imleabhar ≥ 3.67 MΩ -km agus Imleabhar Friotaíocht ≥ 3.67 MΩ -km agus Friotaíocht Imleabhar ≥ 3.67 MΩ -km. Mar thoradh ar fhorbairt mall ar rubar inslithe lasair-saor ó halaigine íseal-halaigine thar na blianta, cé go n-éilíonn ócáidí plódaithe ar nós fobhealaí agus foirgnimh ard-ardú siar lasair fhoriomlán an inslithe cábla agus an tsáraithe chun sábháilteacht dóiteáin a fheabhsú. Leis an teicneolaíocht modhnaithe dromchla de lasair lasair neamhorgánacha amhail hiodrocsaíd alúmanaim agus hiodrocsaíd mhaignéisiam agus taighde agus forbairt modhanna táirgthe nua, is féidir na riachtanais thuas a chomhlíonadh.
1 An éifeacht a bhíonn ag cineálacha lasair neamhorgánacha ar fheidhmíocht an lasair lasair íseal-halaigine íseal-halaigine
Is é neart teanntachta ábhar greamaitheach inslithe EPDM le hiodrocsaíd mhaignéisiam an ceann is mó, go príomha mar gheall ar an bhfíric go bhfuil sé sin
Is éard atá i hiodrocsaíd mhaignéisiam ná criostalach cosúil le snáthaid, méid na gcáithníní níos lú ná 2μm, agus trí mhodhnú gníomhaire cúplála silane chun fórsa ceangailteach agus comhoiriúnacht hiodrocsaíde maignéisiam agus EPDM a fheabhsú. By comparing the oxygen index and vertical combustion grade, it can be seen that the flame retardant effect of magnesium hydroxide is significantly better than that of aluminum hydroxide, this is due to the thermal decomposition temperature of magnesium hydroxide is higher than that of aluminum hydroxide by 140 ℃, which avoids dehydration reaction occurring in advance due to the high temperature of the processing process, moreover magnesium hydroxide will form a layer of oxidized film adsorbed on the surface of the adhesive material after dehydration and promote the formation of charcoal, which will form a layer of hard shell on the surface of the adhesive material In addition, after dehydration, magnesium hydroxide will form a layer of oxidized film adsorbed on the surface of rubber material, and promote the formation of carbón, a chruthaíonn sliogán crua ar dhromchla ábhar rubair, ag aonrú ocsaigine go héifeachtach, rud a fheabhsaíonn an córas lasair lasair. Comparison of volume resistivity can be concluded, aluminum hydroxide on the EPDM insulation rubber Ethylene propylene rubber (EPR), including binary ethylene propylene rubber and ternary ethylene propylene rubber (EPDM) two categories, is a saturated rubber, with excellent electrical insulation, moisture, heat, cold and aging resistance, is widely used in the preparation of wires and cables, and rogha cuimsitheach a bhí ann ar phríomhchorp rubair styrene-butadiene mar ábhar inslithe cábla. With the increasingly high requirements of the laying environment, wire and cable are being developed towards low-smoke halogen-free flame retardant, with the same low-pressure grades of cross-linked polyethylene, EPR also belongs to the flammable materials, its own molecular composition and structure of the flame retardant performance has little effect, only with a considerable amount of flame retardant in order to achieve the purpose of flame retardant, so in order to make Ní féidir ábhair lasair-saor ó halaigine íseal-halaigine a chur leis an aicme lasair lasair saor ó halaigine. Studies have shown that the electrical properties of EPDM is greatly affected by the flame retardant, just add 80 parts of hydroxide flame retardant will make the rapid decline in electrical resistivity, in order to achieve the IEC 60502 ((rated voltage of 1 ~ 30 kV extruded insulated cables and their accessories) standards in the EPR insulating rubber in the normal operation of the conductor at the highest temperature of the insulation Friotaíocht /> 3.67 MΩ -km agus Friotaíocht Imleabhar ≥ 3.67 MΩ -km agus Imleabhar Friotaíocht ≥ 3.67 MΩ -km agus Friotaíocht Imleabhar ≥ 3.67 MΩ -km. Mar thoradh ar fhorbairt mall ar rubar inslithe lasair-saor ó halaigine íseal-halaigine thar na blianta, cé go n-éilíonn ócáidí plódaithe ar nós fobhealaí agus foirgnimh ard-ardú siar lasair fhoriomlán an inslithe cábla agus an tsáraithe chun sábháilteacht dóiteáin a fheabhsú. Leis an teicneolaíocht modhnaithe dromchla de lasair lasair neamhorgánacha amhail hiodrocsaíd alúmanaim agus hiodrocsaíd mhaignéisiam agus taighde agus forbairt modhanna táirgthe nua, is féidir na riachtanais thuas a chomhlíonadh.
1. Tionchar an chineáil lasair neamhorgánach ar fheidhmíocht an lasair íseal-saor ó dheatach-saor ó dheatach Retardant Ábhar Rubber Inslithe EPDM
Is é an neart teanntachta a bhaineann le hábhar greamaitheach inslithe EPDM le hiodrocsaíd mhaignéisiam an ceann is mó, go príomha mar gheall ar an bhfíric go bhfuil hiodrocsaíd mhaignéisiam criostalach cosúil le snáthaid, méid na gcáithníní níos lú ná 2μm, agus trí mhodhnú gníomhaire cúplála silane chun feabhas a chur ar an bhfórsa ceangailteach agus ar chomhoiriúnacht hydroxide agus ar epdm. By comparing the oxygen index and vertical combustion grade, it can be seen that the flame retardant effect of magnesium hydroxide is significantly better than that of aluminum hydroxide, this is due to the thermal decomposition temperature of magnesium hydroxide is higher than that of aluminum hydroxide by 140 ℃, which avoids dehydration reaction occurring in advance due to the high temperature of the processing process, moreover magnesium hydroxide will form a layer of oxidized film adsorbed on the surface of the adhesive material after dehydration and promote the formation of charcoal, which will form a layer of hard shell on the surface of the adhesive material In addition, after dehydration, magnesium hydroxide will form a layer of oxidized film adsorbed on the surface of rubber material, and promote the formation of carbón, a chruthaíonn sliogán crua ar dhromchla ábhar rubair, ag aonrú ocsaigine go héifeachtach, rud a fheabhsaíonn an córas lasair lasair. Is féidir comparáid idir friotachas toirte a thabhairt chun críche, hiodrocsaíd alúmanaim ar an ábhar rubair inslithe EPDM Tá feidhmíocht inslithe leictreach an tionchair i bhfad níos lú ná hiodrocsaíd mhaignéisiam, tá sé seo toisc nach bhfuil seoltacht ATH 104E níos mó ná 60 ps-cm ~; agus gnáth-hiodrocsaíd mhaignéisiam, amhail cineálacha den mhodh táirgthe méine, mar gheall ar fhoinse intíre thionchar an mhianaigh, an t-ábhar neamhíonachta ard, íonacht íseal, chomh maith lena dhromchla le muirear dearfach, polaraíocht ard, strus inmheánach micreascópach, ionas go mbeidh an seoltacht suas le 250 ps-CM. 1 nó níos mó, cuirfidh líon mór hiodrocsaíd mhaignéisiam a chuirtear leis an ábhar rubair EPDM laghdú suntasach ar airíonna inslithe an ábhair rubair, cé gur féidir le hiodrocsaíd mhaignéisiam tar éis cóireála modhnaithe dromchla speisialta feabhas a chur ar airíonna inslithe an ábhair rubair, ach níl na torthaí fós idéalach. Ag cur san áireamh an méid céanna de hiodrocsaíd mhaignéisiam tá airíonna lasair níos fearr ná hiodrocsaíd alúmanaim, déanaimid féin agus monaróirí hiodrocsaíde maignéisiam na táscairí fisiciúla a bhaineann le hiodrocsaíd mhaignéisiam a bharrfheabhsú, na cineálacha de mhionathraitheoirí dromchla agus modhanna táirgthe a tháirgeann, agus a tháirgeann dhá chineál magneium hydroxide atá oiriúnach do tháirgeadh epdm a chur i bhfeidhm. MH3005 agus MH3005 agus MH3005Z.
MH3005 agus MH3005Z Tá friotaíocht ard -toirte ag rubar inslithe EPDM, agus comhlíonann an croí inslithe déanta as rubar MH3005Z go bunúsach riachtanais IEC 60502, ach tá na hairíonna inslithe de rubar MH3005 sách ard. Mar sin féin, tá feidhmíocht inslithe an chroí déanta as rubar MH3005 measartha íseal, agus meastar go ndearnadh damáiste do struchtúr dromchla an chroí le linn an phróisis vulcanization easbhrúite, agus gur gá an chúis a iniúchadh a thuilleadh.
Tríd is tríd, i gcomparáid leis an rubar inslithe EPDM le hiodrocsaíd mhaignéisiam mhodhnaithe ina aonar agus rubar inslithe EPDM le hiodrocsaíd alúmanaim amháin, tá dea -mhaoin lasair, neart teanntachta ard, agus maoine inslithe níos fearr tar éis modhnú dromchla speisialta, ach tá baol ann go bhfuil díghrádú ar mhaoin insulating i gcliabhán inslithe i gcliabhán inslithe i gcliabhán inslithe, agus go bhfuil an t -insuluting maoine atá ró -mharthanach redd redd redd redd redd redd redd redd redd redd go bhfuil sé redd mar go bhfuil sé i bhfearas mar go bhfuil sé i gcroílár, ag magadh go bhfuil sé i bhfearas agus go bhfuil sé i gceist le maoine atá ag teacht le go bhfuil sé mar go bhfuil sé ag déanamh, Is féidir le friotachas na riachtanais a chomhlíonadh fiú gan modhnú.
2. An éifeacht a bhíonn ag retardants lasair neamhorgánacha ar fheidhmíocht na ngreamaitheoirí inslithe lasair íseal-tobac, saor ó halaigine
Úsáid aonair de hiodrocsaíd maignéisiam nó hiodrocsaíd alúmanaim Ní féidir le lasair lasair neamhorgánach riachtanais na n-airíonna leictreacha agus na n-airíonna lasair a chomhlíonadh, mar sin tugann an hiodrocsaíd alúmanaim agus an hiodrocsaíd mhaignéisiam agus a éifeacht ar fheidhmíocht epdm flium-smoke-smoke-fleast-epdm, athanach-smoke-flosat-epdm, athanach-eipeast-eipeastive athanach-smoke-ep-eroulating epdm-eroulative athanach-smoke-smoke-exerantive, athanach-smoke-smoke-ep, athanach-smoke-smoke-ep, athanach-smoke-smoke-ep, MH3005Z dosage de 120 cuid san iomlán, leis an méadú ar an dáileog de MH3005Z, an slaodacht Menni agus neart teanntachta an ghreamaitheora inslithe EPDM, mhéadaigh airíonna lasair lasair, tháinig laghdú ar fhriotaíocht toirte. Leis an méadú ar MH3005Z, méadaíonn slaodacht agus neart teanntachta Menni, méaduithe greamaitheacha inslithe EPDM, méadaíonn an mhaoin lasair lasair, agus laghdaíonn an fhriotaíocht toirte. Nuair a bhíonn an cóimheas idir ATH 104E/MH3005Z 90/30, comhlíonann na hairíonna inslithe agus lasair de ghreamú inslithe EPDM na riachtanais. Comparáid idir ATH 104E / MH3005Z agus an cóimheas idir 110 /10 agus 120 / LO dhá chás, cé gur feabhsaíodh an méadú de 10 gcuid de ATH 104E tar éis na n -airíonna lasair ghreamaitheacha inslithe EPDM, ach airíonna fisiceacha an meath tapa. Lath 104E / MH3005Z agus an cóimheas idir 70/50 agus 70/40 / 40, laghdaíonn sé 10 gcuid de MH3005Z cé gur féidir leis airíonna inslithe an rubair a fheabhsú, ach ní chomhlíonann na hairíonna lasair na riachtanais. D'fhonn airíonna lasair lasair a chinntiú, ní féidir méid iomlán an lasair a laghdú.
Insliú EPDM Ábhar rubair Tá dlús deataigh gan mhais 355 nó mar sin, leis an méid lasair neamhorgánach agus gan aon chaidreamh soiléir leis an gcóimheas, tá sé seo mar gheall ar fhoirmle na gcomhpháirteanna go léir, is é an deatach a fhoirmiú den chuid is mó ná EPDM, cé nach féidir leis an dearadh a dhíscaoileadh a dhíscaoileadh, is féidir leis an dearadh a dhíscaoileadh a fheabhsú trí an t -airíonna flay a fheabhsú trí dheataigh a laghdú, is féidir leis an dearadh a laghdú an t -airíonna a laghdaíonn an t -airíonna flame a laghdaíonn an t -airíonna a laghdaíonn an t -airíonna a laghdaíonn an t -airíonna a laghdaíonn an t -airíonna a laghdaíonn an t -airíonna flame is féidir leis an airíonna a laghdú an t -airíonna a fhéadann an t -abhcóide is féidir a dhéanamh le hairíonna an t -am ar fad a dhéanamh is féidir le dóchán ábhair.
3. Gníomhaire laghdaithe deataigh ar fheidhmíocht comhdhúil inslithe inslithe lasair-saor ó halaigine íseal-halaigine
JB / T 10707-2007 'Éilíonn' teirmeaplaisteacha saor ó halaigine íseal ábhair chábla lasair 'nár chóir go mbeadh dlús deataigh gan mhaolú an ábhair rubair níos mó ná 250, chun dlús deataigh an ábhair rubair a laghdú leis an gcontúirt deataigh. Cuimsíonn Montmorillonite Montmorillonite-bhunaithe cailciam-bhunaithe, bunaithe ar mhaignéisiam-bhunaithe, tar éis stripping agus scaipeadh, íonú agus modhnú, ilchodach orgánach speisialta, is é meán tiús an chiseal ná 25 nm. Roghnaítear Montmorillonite chun éifeacht deataigh níos fearr a bhaint amach.
Montmorillonite ar an ábhar rubair inslithe EPDM Tá dlús deataigh an tionchair an -soiléir, ach is féidir leis a bheith ina mhéadú beag ar airíonna lasair lasair, cé go mbíonn tionchar níos lú ag airíonna eile; Leis an méadú ar mhéid Montmorillonite, laghdaíodh de réir a chéile, agus is gnách go ndéantar cobhsú, ag cur na bhfachtóirí costais san áireamh, ag cur na fachtóirí costais san áireamh, roghnaigh an méid Montmorillonite ar feadh 5 chuid.
4 Conclúid
.
.
.