GA-91X0 a ni.
Herchy a ni a .
A awm theihna: | |
---|---|
A tam ber: | |
Test: Curing agent 1% (Silicone gum-a DBPMH paste 50%), 175° x5minx15mpa
Product Parameters 1000 a ni. | |||||
Thilsiam | GA-9130 a ni. |
GA-9140 a ni. | GA-9150 a ni. | GA-9160 a ni. | GA-9170 a ni. |
Landan | Translucent 1000 a ni. | ||||
Williamplasticity . |
150 |
190 |
250 |
280 |
300 |
Harsatna (Shorea) . |
30 |
40 |
50 |
60 |
70 |
Density(G/CM3) a ni. | 1.11 |
1.14 |
1.17 |
1.20 |
1.21 |
Tensile chakna (MPA) . |
8.0 |
9.5 |
10.0 |
9.0 |
8.5 |
Elongation(%) . | 900 |
700 |
600 |
500 |
400 |
Tear chakna (kn/m) . | 17 |
20 |
25 |
25 |
25 |
A chung lam do theihna(Ω) . | 1011 |
Test: Curing agent 1% (Silicone gum-a DBPMH paste 50%), 175° x5minx15mpa
Product Parameters 1000 a ni. | |||||
Thilsiam | GA-9130 a ni. |
GA-9140 a ni. | GA-9150 a ni. | GA-9160 a ni. | GA-9170 a ni. |
Landan | Translucent 1000 a ni. | ||||
Williamplasticity . |
150 |
190 |
250 |
280 |
300 |
Harsatna (Shorea) . |
30 |
40 |
50 |
60 |
70 |
Density(G/CM3) a ni. | 1.11 |
1.14 |
1.17 |
1.20 |
1.21 |
Tensile chakna (MPA) . |
8.0 |
9.5 |
10.0 |
9.0 |
8.5 |
Elongation(%) . | 900 |
700 |
600 |
500 |
400 |
Tear chakna (kn/m) . | 17 |
20 |
25 |
25 |
25 |
A chung lam do theihna(Ω) . | 1011 |