GA-2720
Nws li
Muaj Qhov Muaj: | |
---|---|
Quatity: | |
Kuaj: A / B piv ntawm 1: 1, 130 ° C x 5min X 15MPA
Cov khoom tsis muaj | |||||||
Khoom | GA-2720 | GA-2730 | GA-2740 | GA-2750 | GA-2760 | GA-2770 | |
Kev tshwm sim | Dawb vog | ||||||
Viscosity (PA.S) |
2000 | 3000 | 3000 | 3500 |
4000 | 5000 |
|
Hardness (Shorea) | 20 | 30 | 40 | 50 |
60 |
70 |
|
Ntom ntom (G / cm3) | 1.10 | 1.10 | 1.11 | 1.12 | 1.1.3 |
1.14 |
|
Tensile lub zog (mpa) | 7.0 |
8.0 |
9.5 |
10.0 |
10.0 |
9.5 |
|
Elongation (%) | 880 | 800 | 700 | 550 | 500 |
350 |
|
Kua Muag Lub Zog (Kn / M) | 16 | 30 | 35 |
40 | 35 |
30 |
|
Linearshrinkage (%) | 2.1 | 2.1 | 2.1 | 2.0 | 2.0 |
2.0 |
Kuaj: A / B piv ntawm 1: 1, 130 ° C x 5min X 15MPA
Cov khoom tsis muaj | |||||||
Khoom | GA-2720 | GA-2730 | GA-2740 | GA-2750 | GA-2760 | GA-2770 | |
Kev tshwm sim | Dawb vog | ||||||
Viscosity (PA.S) |
2000 | 3000 | 3000 | 3500 |
4000 | 5000 |
|
Hardness (Shorea) | 20 | 30 | 40 | 50 |
60 |
70 |
|
Ntom ntom (G / cm3) | 1.10 | 1.10 | 1.11 | 1.12 | 1.1.3 |
1.14 |
|
Tensile lub zog (mpa) | 7.0 |
8.0 |
9.5 |
10.0 |
10.0 |
9.5 |
|
Elongation (%) | 880 | 800 | 700 | 550 | 500 |
350 |
|
Kua Muag Lub Zog (Kn / M) | 16 | 30 | 35 |
40 | 35 |
30 |
|
Linearshrinkage (%) | 2.1 | 2.1 | 2.1 | 2.0 | 2.0 |
2.0 |