Wani lokacin masu amfani zasu iya tambayar tsawon lokacin da za'a iya jan tsawon lokacin da fili mai rikicewa ba tare da fashewa ba. Wannan wani muhimmin kayan abu ne a cikin gwajin daidaitaccen yanayi kamar yadda Astm da ISO. Abubuwan da ke biye na iya taimaka wa wadanda suka dace da bukatun mai amfani.

1. SBR

SBR polymerized by emulsion at -10 ° C zai iya ba da fili mafi kyau ta elongation.

2. Nr

Daga cikin sassan daban-daban na NR, an filastik roba na roba mai narkewa mai narkewa yana da mafi girman elongation na zamani.

3. Neopene da masu zane

A cikin neprene forulations, inorganic flers tare da babban barbashi maimakon ƙwararrun size ya kamata a yi amfani da shi don inganta elongation na tenal hutu. Bugu da kari, maye gurbin karfafa carbon baƙar fata mai baƙar fata tare da baƙar fata mai launin fata na iya inganta elongation na hutu na tishon.

4. TPE da TPV

Thermoplastic ellastorst da thermoplaastic Volcanizates etcanizes antacceropics antacceropic, musamman don allurar da ke da yawa elong da ƙarfi da ƙarfi da ƙarfi sun dogara da jagorancin tafiyarsu.

5. Carbon baki

Amfani da carbon baƙar fata tare da ƙaramin yanki da ƙananan tsari da rage tsari da rage cika adadin carbon baƙar fata na iya inganta elongation na fili.

6. Farcum foda

Sauya adadin adadin carbon tare da ƙwararrun ƙwaya mai girman talabi na iya inganta elongation elongation na fili, amma ba shi da ƙarancin tasiri a kan ƙarfin da zai iya ƙara modulus a cikin low iri.

7. Sulfur Vulcization

Fa'idodin sulfur idan aka kwatanta da peroxide rashin daidaituwa shine cewa zai iya sa kayan roba suna da elong mai girma. Gabaɗaya, tsarin tsarin sulfur na iya ƙaddamar da mafi kyawun elongation zuwa fili fiye da tsarin ƙananan sulfur.

8. Gel

Roba mai ban sha'awa kamar SBR gabaɗaya yana ɗauke da ƙuduri. Koyaya, hada haduwa da sbr a yanayin zafi sama da 163 ° C na iya samar da kwalliya masu sako-sako (wanda za'a iya birgima a bude kuma ba za a yi birgima a cikin wasu abubuwan sha ba). Dukansu gels suna rage elongation na tenangin na fili, don haka zazzage zafin jiki na SBR dole ne a kula da shi da taka tsantsan.

9. Haɗawa

Haɓaka inganta watsawa na carbon baƙar fata, wanda ke taimakawa haɓaka elongation na tenonile na fili.

10. Tasiri da nauyin kwayoyin

Don NBR raw roba, da amfani da dankalin turawa mara amfani da ƙarancin ƙwayoyin cuta na iya inganta elongation na hutu na tisile. Emulsion sbr, narkar da SBR, Br da Ima kuma sun dace da wannan.

11. Digiri na Vulcanization

Gabaɗaya, ƙarancin digiri na Vulcanization na iya haifar da babban resile elongation na fili.