ʻO SABIC EPDM 855 kahi mooney viscosity kiʻekiʻe, medium ethylene a me ENB content grade i hana ʻia e ka polymerization solution me ka hoʻohana ʻana i ka metallocene catalyst. He polimer amorphous me ka puunaue kaumaha molekala. Loaʻa ia i nā bale friable.

Waihoʻoluʻu: ʻEleʻele
Paʻakikī: 75-85 Shore A
Vulcanization system: sulfur system
Raw rubber acrylonitrile content: 35±3%
Size: hiki ke hoʻopilikino ʻia (strip or wide)
Nā kūlana Vulcanization: 170 ° C * 10min lua vulcanization: 150 ° C * 4h (2mm standard test piece)
MOQ: 50kg.

Waihoʻoluʻu:
ʻEleʻele Paʻa: 55-65 Shore A
Vulcanization system: sulfur system
Raw rubber acrylonitrile content: 43±3%
Size: hiki ke hoʻopilikino ʻia (strip or wide)
Nā kūlana Vulcanization: 170 ° C * 10min lua vulcanization: 150 ° C * 4h (2mm standard test piece)
MOQ: 50kg.

Kala: ʻEleʻele Nui
: hiki ke hoʻopilikino ʻia (ka ʻāpana a ākea paha)
Nā kūlana Vulcanization: 170 ° C * 10min (2mm specimen maʻamau)
MOQ: 50kg

Waihoʻoluʻu:
ʻEleʻele Paʻa: 55-65 Shore A
Vulcanization system: sulfur system
Raw rubber acrylonitrile content: 35±3%
Size: hiki ke hoʻopilikino ʻia (strip or wide)
Nā kūlana Vulcanization: 170 ° C * 10min lua vulcanization: 150 ° C * 4h (2mm standard test piece)
MOQ: 50kg.

Ka waihoʻoluʻu: Green (customizable)
Pūnaehana Vulcanization: peroxide system
Fluorine content: 68%
Mooney viscosity: ML (1 + 10) 121 ° C 35-55
Nui: Hiki ke hoʻololi hou aku (pepa) Nā kūlana Vulcanization: 175 ° C * 10min Ka lua o ka vulcanization
202 ° Q * 4hmen maʻamau
: