Lanu: Uliuli (fa'atonu)
foliga vaaia: ta'avale (fa'atonu)
Ituaiga Vulcanization: peroxide
Mooney viscosity ML(1+4)100℃：75-85
Malosi:60±5 Shore A
Malosi fa'amama: min.10 Mpa
Fa'aumi ile malologa:min.300% MOQ:
150kg .
Tolu masina e muta ai:

Ethylene propylene pa'u o se pa'u gaosia ma ethylene ma propylene o le monomer autu, e tusa ai ma le tuufaatasiga eseese o le monomer i le filifili mole, o loʻo i ai binary ethylene propylene rubber (EPM) ma le tertiary ethylene propylene rubber (EPDM), E masani ona faʻaaogaina i vaega taʻavale, mea e le susu mo le fausiaina, vevela ma uaea faʻapipiʻi faʻapipiʻi. mea faaopoopo ma isi oloa.

Lanu: Felanulanua'i (fa'atonu)
foliga: Poloka po'o fasipepa (fa'apipi'i)
Ituaiga Vulcanization: peroxide
Mooney viscosity ML(1+4)100℃：45-55
Malosi:60±5 Shore A
Malosi fa'amama: min.10 Mpa
Elongation i le malologa：min.300%
MOQ:
1.

Lanu: Lanu uliuli (fa'atonuina)
foliga vaaia: Poloka po'o fasi pepa (fa'atonu)
Ituaiga Vulcanization: peroxide
Mooney viscosity ML(1+4)100℃：55-65
Malosi:60±5 Shore A
Malosi fa'amama: min.10 Mpa
Elongation i le malologa:min.300%
MOQ
aso e muta: 15kg.

Lanu:
Lanu uliuli: Poloka po'o fasipepa (fa'apipi'i)
Ituaiga Vulcanization: Sulfur
Mooney viscosity ML(1+4)100℃：45-55
Malosi:60±5 Shore A
Malosi fa'amama: min.10 Mpa
Elongation i le malologa:min.300%
MOQ: 150kg
Aso e muta: tasi le masina

Lanu: Lanu uliuli (fa'atonuina)
foliga vaaia: Poloka po'o fasi pepa (fa'apipi'i)
Ituaiga Vulcanization: peroxide
Mooney viscosity ML(1+4)100℃：65-75
Malosi:60±5 Shore A
Malosi fa'amama: min.10 Mpa
Elongation i le malologa:min.300%
MOQ
aso e muta: 15kg.