Lokola lolenge ya caoutchouc non polaire na chaîne principale saturée, caoutchouc ya propylène éthylène ezali na performance excellente na résistance na météo, résistance na media polaire, résistance na vieillissement, résistance na ozone, etc. Kasi, ezali na ba grades ebele ya caoutchouc ya propylène éthylène. However, there are many grades of ethylene propylene rubber, different grades of ethylene propylene rubber with different ethylene content, third monomer type and content, mooney viscosity, etc. In order to facilitate the technicians to choose the appropriate grade of ethylene propylene rubber, this paper selects a few typical types of the ENB type ethylene propylene rubber which is the most widely used in the industry, and makes a certain study on the effects of Contenu ya éthylène, teneur ya troisième monomère mpe viscosité ya Mooney na performance ya matériel. Bolukiluki moko boye esalemi, oyo ezali na mwa ntina oyo ezali kotambwisa.
Na bokeli ya tekiniki mpe ya lisanga, bosenga ya bato mpo na biloko ya langi ya pete ezali mpe kobakisama, biloko ya caoutchouc ya langi ya pete mpe ya langi ezali kokota mokemoke na bomoi ya bato, silice lokola agent ya ntina ya kolendisa mpo na biloko ya caoutchouc ya langi ya pete ezali kosala mosala ya ntina mingi.
Lokola agent ya renforcement oyo basalelaka mingi mingi na ba produits ya caoutchouc ya couleur légère, silice ezali ko jouer un rôle de plus en plus important.
Ba résultats mpe masolo .
1 Performance ya vulcanisation ya caoutchouc ya propylène éthylène différent .
Effet ya teneur ya éthylène na temps ya kozika (TC10) mpe na positivité ya procédé ya caoutchouc ya propylène ya éthylène.
(The effect of ethylene content on the curing time of ethylene propylene rubber (tc10) and process vulcanization time (tc90) is large, with the increase of ethylene content, the tc10 and tc90 of the material are shortened gradually, the content of the third monomer also has a certain effect on the tc10 and tc90, when the material is close to the same content of ethylene or the Ndenge moko mpe soki monomère ya misato ezali na nse, TC10 mpe TC90 ya matériel ezali mokuse; Couple minimum (mL) ya matériel, ezali na nse ya contenus ya monomère ya misato.
The minimum torque (ML) of the material is mainly affected by the ethylene content, the higher the ethylene content, the greater the ML of the material, the worse the mobility at the beginning of vulcanization, because the maximum torque (MH) can reflect the modulus of the rubber, it can be seen that with the increase of ethylene content, the modulus of the rubber also increases gradually, the third monomer content on the modulus of the material is Proportionnel positif na contribution ya teneur ya troisième monomère ezali plus contenus ya matériel, soki module ya matériel ezali munene, module ya matériel ekozala munene, module ya matériel ekozala monene. Mpo na kozala na éthylène moko to ya ndenge moko, soki monomère ya misato ezali mingi, soki module yango ekozala mingi. Bokeseni kati na couple ya likolo mpe couple ya nse (MH -mL) esalelamaka mpo na kopesa bizaleli ya degré ya réticulation ya matériel ya caoutchouc, mpe ekoki komonana ete contenus ya éthylène mpe monomère ya misato ezali na effet moko na degré ya réticulation, soki ezali na contenus ya éthylène mingi soki degré ya interliseur ezali monene, mpe na kati ya monomer ya likolo, oyo ezali mpe likolo.
2 Propriétés mécaniques ya ba recherches ya caoutchouc ya propylène éthylène différents .
Bokasi ya caoutchouc ezali mingimingi kotungisama na teneur ya éthylène, soki ezali na éthylène mingi, makasi ya caoutchouc ekozala mingi, monomère ya misato ezali na bopusi moke likoló na makasi; material tensile strength and tear strength by ethylene is more obvious, with the increase of ethylene content, the material tensile strength and tear strength are gradually increased, when the ethylene content is similar or the same, the higher the third monomer content, the higher the material tensile strength and tear strength, indicating that ethylene content is the same, the higher the material tensile strength, the higher the material tensile strength, the higher the material tensile strength, the higher the Bokasi ya traction ya matériel, makasi ya traction ya matériel ekozala likolo, makasi ya traction ya matériel ekozala likolo mpe makasi ya mayi ya miso. Ndenge moko mpe, soki monomère ya misato ezali na likoló mingi, makasi ya kokangama mpe makasi ya kopasola ya eloko yango ezali likoló, yango emonisi ete motuya ya éthylène mpe monomère ya misato ezali na makasi ya bopusi ya effet synergique; Contenu d’éthylène et le troisième teneur des monomères de la stress de étirement matériel ezali ndenge moko na impact na force ya matériel, plus teneur ya éthylène ya matériel ezali likolo, plus ya troisième monomère ya stress ya traction ya matériel ekozala likolo mingi koleka; Contenu d’éthylène ya elongation ya traction ya effet ya moke, na kati ya gamme moko boye ya elongation ya traction ya matériel na bomati ya teneur ya éthylène, na point moko boye, makasi ya traction mpe makasi ya mayi ya miso ya matériel ezali komata mokemoke, na point moko boye, plus ya troisième monomère. Na kati ya intervalle moko boye, elongation na rupture emati mokemoke na bomati ya contenus basé na éthylène, mpe na sima ebandi kokita mokemoke sima ya degré moko boye, contenus ya monomere ya misato ezali inversement proportionnel na changement ya elongation na rupture, mpo na contenus moko to ya ndenge moko oyo esalemi na éthylène, se contenus ya monomère ya misato ezali, plus grande elongation ezali; Bosali ya abrasion ya matériel ezali na boyokani monene na bokasi mpe makasi na yango, na lolenge ya monene, makasi mpe makasi ekozala likolo, volume ya abrasion ekozala moke na kolanda yango, mpe performance ya abrasion ekozala malamu koleka; Lokola contenus oyo esalemi na éthylène ezali komata, ezali na boyokani moko boye kati na makasi mpe makasi mpe performance ya abrasion ya matériel. Durcissement ya matériel mpe makasi ezali na degré moko boye ya augmentation, volume abrasif ekiti mokemoke, ba côtés mibale ya troisième contenus ya monomère ekozala mpe na effet na ba propriétés abrasives ya matériel, oyo emonisami na augmentation ya troisième monomère teneur, eko réduire volume abrasif ya matériel, kasi soki tokokanisi yango na effet ya teneur éthylène, contenus ya troisième monomère ezali na impact moke na ba propriétés abrasives na yango.
3 différents éthylène propylène caoutchouc résistant à chaleur à chaleur Performance ya vieillissement .
Ekoki komonana ete, nsima ya konuna na 160 °C na boumeli ya 24h, makasi ya biloko ebongwanaka moke mpenza, mpasi ya kokangama ya ntango nyonso emati mwa moke, kasi mbangu ya kobatela mobimba ezali mingi, makasi ya kokangama ekiti mwa moke, taux ya retention mobimba etikali mingi, mpe taux ya elongation ya tensile ebongwani mwa moke; Yango ezali bongo mpamba te caoutchouc ya éthylène-propylène ezali caoutchouc oyo ezali na chaîne principale saturée, oyo ezali na résistance ya vieillissement ya chaleur ya likolo. Na ntina na résistance excellente ya vieillissement ya mopepe ya moto ya caoutchouc ya propylène éthylène, ezali pasi kolakisa effet ya teneur ya éthylène mpe teneur ya troisième monomère na performance ya vieillissement ya matériel na période mokuse ya vieillissement ya mopepe ya moto.
4 différents éthylène propylène caoutchouc résistance na température ya nse .
Na bomati ya teneur ya éthylène, résistance ya température ya moke ya matériel ebebisaka mokemoke.
Na bomati ya teneur ya éthylène, résistance ya température ya nse ya matériel ebebi mokemoke, teneur ya éthylène moko to ya ndenge moko, soki teneur ya monomère ya misato ezali moke, résistance ya température ya se ya matériel ekozala malamu, yango ezali mpo ete contenu ya éthylène ya caoutchouc ya propylène ya éthylène ekomata, degré ya régularité moléculaire ekozala likolo mpe ya likolo, mpe na macro-aize ya ba macross, mpe na ba macross, mpe na makoki ya ba macros, mpe na makoki ya ba macros, mpe na makoki ya ba macros, mpe na ba macross, mpe na ba macros, mpe na makoki ya ba macros, mpe na makoki ya ba macros, mpe na makoki ya ba macros, mpe na makoki ya ba macros, mpe na makoki ya ba macros, mpe na makoki ya ba macros, mpe na makoki ya ba macros, mpe na makoki ya ba macros, mpe na makoki ya ba macroses. Bomati ya makoki ya cristallisation ekosala ete bomati mpe makasi ya matériel emata, kasi ekokitisa mpe flexibilité ya chaîne moléculaire na mobimba na yango, mpo ete résistance ya température ya moke ya matériel ebeba. Tango contenus ya groupe ya éthylène ezali pene moko na mosusu, contenu ya monomère ya misato ya se ekosala que degré ya se ya réticulation ya matériel, oyo ekomatisa flexibilité ya molécule na mobimba na yango, mpe ekobongisa résistance ya température ya moke ya matériel.
Maloba ya nsuka
(1) Ba grades ndenge na ndenge ya caoutchouc ya propylène éthylène, contenu na yango ya éthylène ezali na influence monene na ba aspects nionso ya performance, elandi na teneur ya monomère na yango ya misato, Viscosité ya Mooney ezali na influence monene na performance na yango ya traitement, mpe ezali na influence moke na ba propriétés mosusu.
(2) Mpo na lolenge moko ya misato ya monomère mpe na kati ya caoutchouc ya propylène ya éthylène, soki ezali na éthylène mingi, makasi ya mécanique ekozala mingi, résistance ya molunge mpe ya bobange ya mopepe ekozala malamu, kasi résistance na yango na performance ya température ya nse ezali malamu te.